Abstract Acrylonitrile/vinyl acetate/styrene copolymers containing a high proportion of acrylonitrile (50-80% by weight) which undergo no discoloration and result in highly transparent products when thermoplastically processed are produced by continuous emulsion copolymerization the monomers in a tube reactor in which comparatively little back mixing occurs (plug flow = laminar flow = non-stationary state). A seed latex having a specified, small particle size with a narrow particle size distribution of the copolymer is obtained; the reaction mixture is then cooled, if necessary, in order to prevent further polymerization as far as possible and continuously transferred into a stirrer vessel while at the same time a stream of monomers consisting of acrylonitrile, vinyl acetate and styrene also having a specified but different percentage composition of monomers than in stage 1 is also fed into this stirrer vessel, and in this second stage of the process, polymerization is carried out at specified temperatures and with specified residence times under stationary conditions, i.e. with back mixing up to a total conversion of 70 to 90%.
Mixtures of acrylonitrile/vinyl acetate/styrene terpolymers comprising (A) 10 to 30% by weight of a terpolymer of copolymerised units of acrylonitrile, vinyl acetate and styrene with weight averages of the composition Ew, standard deviation δw and skewness of distribution Ωw as follows: ______________________________________
Ew.sup.-- δw Ωw
______________________________________
Acrylonitrile
50-85% by wt.
6-20% by wt. -0.8 to 0.5
Vinyl acetate
10-26% by wt.
3-10% by wt. -0.5 to 0.4
Styrene 5-24% by wt.
5-30% by wt. -0.5 to 0.8
______________________________________ and a K-value of 50 to 70 measured at 25° C. in a 0.5% by weight dimethylformamide solution, and (B) 70 to 90% by weight of a terpolymer of copolymerised units of acrylonitrile, vinyl acetate and styrene with weight averages of the composition E'w, standard deviation δ'w and skewness of distribution Ω'w as follows ______________________________________
E'w.sup.-- δ'w Ω'w
______________________________________
Acrylonitrile
50-85% by wt.
0-2.0% by wt.
0
Vinyl acetate
6-30% by wt. 0-1.0% by wt.
0
Styrene 9-20% by wt. 0-1.0% by wt.
0
______________________________________ and a K-value of 55-70 measured at 25° C. in a 0.5% by weight dimethylformamide solution, with the proviso that the difference between the styrene contents Ew and E'w does not exceed 4% by weight and the K-values of the terpolymers A and B differ from each other by at the most 10.
Claim 2
Dependent Claim
216 words
Mixtures of acrylonitrile/vinyl acetate/styrene terpolymers comprising (A) 10 to 30% by weight of a terpolymer of copolymerised units of acrylonitrile, vinyl acetate and styrene with weight averages of the composition Ew, standard deviation δw and skewness of distribution Ωw as follows: ______________________________________
Ew.sup.-- δw Ωw
______________________________________
Acrylonitrile
50-85% by wt.
6-20% by wt. -0.8 to 0.5
Vinyl acetate
10-26% by wt.
3-10% by wt. -0.5 to 0.4
Styrene 5-24% by wt.
5-30% by wt. -0.5 to 0.8
______________________________________ and a K-value of 50 to 70 measured at 25° C. in a 0.5% by weight dimethylformamide solution, and (B) 70 to 90% by weight of a terpolymer of copolymerised units of acrylonitrile, vinyl acetate and styrene with weight averages of the composition E'w, standard deviation δ'w and skewness of distribution Ω'w as follows ______________________________________
E'w.sup.-- δ'w Ω'w
______________________________________
Acrylonitrile
50-85% by wt.
0-2.0% by wt.
0
Vinyl acetate
6-30% by wt. 0-1.0% by wt.
0
Styrene 9-20% by wt. 0-1.0% by wt.
0
______________________________________ and a K-value of 55-70 measured at 25° C. in a 0.5% by weight dimethylformamide solution, with the proviso that the difference between the styrene contents Ew and E'w does not exceed 4% by weight and the K-values of the terpolymers A and B differ from each other by at the most 10.