Hydrogenation process of olefin polymers for producing white oils
Assignee: Labofina SA
•
Filing: 1977-03-15
•
Granted: 1978-07-18
•
Expires: 1997-03-15
Abstract
Abstract A process for hydrogenating polymers which are derived from olefin units containing 4 carbon atoms is disclosed whereby white oils which exhibit a low iodine value (e.g., below 0.26) are obtained under relatively mild reaction conditions. The hydrogenation is effected in the presence of a catalyst comprising palladium on a bimodal alumina support ehibiting a total pore volume of at least 0.25 ml/g of which 35 to 50% are provided by small pores the mean size of which is below 300A and 25 to 35% are provided by large pores the mean size of which is above 300A and is at least 1.5 times the mean size of the small pores.
Inventors
- 👤 Guy F. S. Debande
- 👤 Raymond N. M. Cahen
- 👤 Jacques F. J. Grootjans
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:44
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
188 words
A process for hydrogenating a liquid polymer derived from olefin units containing 4 carbon atoms, which comprises the step of hydrogenating said polymer at a hydrogen pressure of between about 20 and about 120 kg/cm 2 , a liquid hourly space velocity of between about 0.25 and 4 hr -1 , a hydrogen:polymer ratio of between about 250 and 6,000 Nl/l, and at a temperature of between about 130° and about 250° C in the presence of a catalyst comprising palladium on an alumina support, said support exhibiting a total pore volume of from about 0.25 ml/g to about 2.5 ml/g, wherein about 35 to about 50% of said pore volume is provided by small size pores having a pore size distribution lower than about 300A and about 25 to about 35% of said pore volume is provided by large size pores having a pore size distribution higher than about 300A and wherein the pore size distribution of the large size pores is at least 1.5 times that of the small size pores, whereby a white oil having an iodine number of less than about 0.26 is obtained.
Claim 2
Dependent Claim
188 words
A process for hydrogenating a liquid polymer derived from olefin units containing 4 carbon atoms, which comprises the step of hydrogenating said polymer at a hydrogen pressure of between about 20 and about 120 kg/cm 2 , a liquid hourly space velocity of between about 0.25 and 4 hr -1 , a hydrogen:polymer ratio of between about 250 and 6,000 Nl/l, and at a temperature of between about 130° and about 250° C in the presence of a catalyst comprising palladium on an alumina support, said support exhibiting a total pore volume of from about 0.25 ml/g to about 2.5 ml/g, wherein about 35 to about 50% of said pore volume is provided by small size pores having a pore size distribution lower than about 300A and about 25 to about 35% of said pore volume is provided by large size pores having a pore size distribution higher than about 300A and wherein the pore size distribution of the large size pores is at least 1.5 times that of the small size pores, whereby a white oil having an iodine number of less than about 0.26 is obtained.
Claim 3
Dependent Claim
27 words
The process as defined in claim 1, wherein the polymers are selected from the group consisting of butene polymers, isobutene polymers and copolymers of butene and isobutene.
Claim 4
Dependent Claim
21 words
The process as defined in claim 2, wherein the molecular weight of the polymer is between about 300 and about 2,000.
Claim 5
Dependent Claim
21 words
The process as defined in claim 1, wherein the catalyst contains between about 0.25 and about 1.5% by weight of palladium.
Claim 6
Dependent Claim
20 words
The process as defined in claim 4, wherein the catalyst contains between about 0.4 and 0.9% by weight of palladium.
Claim 7
Dependent Claim
47 words
The process as defined in claim 1, wherein the catalyst support comprises a bimodal alumina wherein the small pores have a pore size distribution of between about 30 and about 300A and the large pores have a pore size distribution of between about 300A and about 150,000A.
Claim 8
Dependent Claim
23 words
The process as defined in claim 6, wherein the pore size distribution of the small pores is between about 50 and about 150A.
Claim 9
Dependent Claim
29 words
The process as defined in claim 6, wherein said pore volume provided by the small pores is at least equal to said pore volume provided by the large pores.
Claim 10
Dependent Claim
23 words
The process as defined in claim 6 wherein the shape of the catalyst support is consists of extrudates in the form of cylinders.
Claim 11
Dependent Claim
14 words
The process as defined in claim 9, wherein the catalyst support is a powder.
Claim 12
Dependent Claim
13 words
The process as defined in claim 9, wherein the catalyst is a granulate.
Claim 13
Dependent Claim
17 words
The process as defined in claim 6 wherein the shape of the catalyst support consists of beads.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |