US4098728A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Medical surgical sponge and method of making same
Assignee: MEROCEL Corp A CORP OF CONNECTICUT
•
Filing: 1976-01-02
•
Granted: 1978-07-04
•
Expires: 1996-01-02
Abstract
Abstract A uniformly expandable hydrophilic sponge, adapted for medical usage, characterized by instantaneous wicking and a high liquid holding capacity comprising a reaction product of polyvinyl alcohol and formaldehyde. The wicking and liquid holding capacity is attained by controlling the time, temperature and processing conditions while forming and curing the reaction product in an aqueous medium. The sponge is rendered uniformly expandable by drying the wet sponge while maintaining the shape of the wet sponge. The sponge can be made X-ray opaque by incorporating, homogeneously, throughout an encapsulated radiopaque substance with the formaldehyde and polyvinyl alcohol. The sponge is biocompatible, non-toxic, lint free, compressible, resilient, strong, non-abrasive, free of foreign leachable materials and is of exceptionally high fluid holding capacity.
Inventors
- 👤 Solomon Rosenblatt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 23:20
CPC Classifications
A; A61; A61L; A61L15/00; A61L15/16; A61L15/42; A61L15/425; A61L15/60; Y; Y10; Y10S; Y10S521/00; Y10S521/905
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
87 words
A biocompatible, polymeric, elastomeric, lint-free, uniformly swellable hydrophilic sponge for medical purposes having a uniform pore geometry and pore size distribution throughout its volume comprising the inorganic acid-catalyzed reaction product of formaldehyde and polyvinyl alcohol, said sponge being characterized by an initial water absorbtion and a wicking point of a maximum of 10 seconds of contact with the body fluid and by a variation in the size of the diameter of the pores of less than about 8 to 1 as determined by a stereoscopic microscope eyepiece.
Claim 2
Dependent Claim
87 words
A biocompatible, polymeric, elastomeric, lint-free, uniformly swellable hydrophilic sponge for medical purposes having a uniform pore geometry and pore size distribution throughout its volume comprising the inorganic acid-catalyzed reaction product of formaldehyde and polyvinyl alcohol, said sponge being characterized by an initial water absorbtion and a wicking point of a maximum of 10 seconds of contact with the body fluid and by a variation in the size of the diameter of the pores of less than about 8 to 1 as determined by a stereoscopic microscope eyepiece.
Claim 3
Dependent Claim
13 words
The sponge of claim 1 which contains a water-swellable non-toxic polymeric gelling agent.
Claim 4
Dependent Claim
11 words
The sponge of claim 1 which contains a biodegradable accelerating agent.
Claim 5
Dependent Claim
26 words
The sponge of claim 1 wherein said sponge is characterized by an absorption capacity for liquids in excess of twenty times the weight of the sponge.
Claim 6
Dependent Claim
125 words
A biocompatible, polymeric, elastomeric, lint-free, uniformly swellable hydrophilic sponge for medical purposes having a uniform pore geometry and pore distribution throughout its volume comprising the inorganic acid-catalyzed reaction product of formaldehyde and polyvinyl alcohol, said sponge being characterized by an initial water absorption and wicking point of a maximum of 10 seconds of contact with the body fluid, and by a variation in the size of the diameter of the pores of less than about 8 to 1 as determined by a stereoscopic microscope eyepiece and said sponge containing a homogeneously distributed particulate radiopaque material having a coating of polyvinyl alcohol or a reaction product of polyvinyl alcohol and formaldehyde which coating is copolymerized with said acid-catalyzed reaction product of formaldehyde and the polyvinyl alcohol.
Claim 7
Dependent Claim
125 words
A biocompatible, polymeric, elastomeric, lint-free, uniformly swellable hydrophilic sponge for medical purposes having a uniform pore geometry and pore distribution throughout its volume comprising the inorganic acid-catalyzed reaction product of formaldehyde and polyvinyl alcohol, said sponge being characterized by an initial water absorption and wicking point of a maximum of 10 seconds of contact with the body fluid, and by a variation in the size of the diameter of the pores of less than about 8 to 1 as determined by a stereoscopic microscope eyepiece and said sponge containing a homogeneously distributed particulate radiopaque material having a coating of polyvinyl alcohol or a reaction product of polyvinyl alcohol and formaldehyde which coating is copolymerized with said acid-catalyzed reaction product of formaldehyde and the polyvinyl alcohol.
Claim 8
Dependent Claim
185 words
The process for forming the sponge of claim 1 which comprises frothing a mixture of medium molecular weight polyvinyl alcohol, an inorganic acid and a non-toxic wetting agent at a temperature of about 85°-140° F. to form an elevated temperature froth having a volume between 150 and 400% of the unfrothed mixture; adding to said elevated temperature froth, an aqueous solution of formaldehyde at about 85°-140° F., the amount of formaldehyde being that sufficient to react with between about 25 and 55% of the hydroxyl groups of the polyvinyl alcohol, and frothing the resulting mixture at said elevated temperature until the mix becomes noticeably thicker to form a pourable and extrudeable froth having a mechanical stability sufficiently strong to substantially maintain the volume of the froth; maintaining the resulting froth at about 140°-170° F. until the exterior portion thereof cures and then maintaining the exterior cured froth at about 80°-140° F. to complete the curing, whereby a sponge is formed; eluting substantially all of the elutable acid, wetting agent and formaldehyde from said sponge; and heating the eluted sponge to dryness while maintaining its shape.
Claim 9
Dependent Claim
16 words
The process of claim 6 wherein oversized bubbles are removed from the froth prior to curing.
Claim 10
Dependent Claim
26 words
The process of claim 6 wherein prior to heating to dryness, the eluted sponge is frozen, cut into smaller sponges, and the smaller sponges are rewashed.
Claim 11
Dependent Claim
21 words
The process of claim 8 wherein the temperature during both of said frothing steps is between about 120° and 130° F.
References Cited (Backward Citations)
US2609347A
Cited
US2664367A
Cited
US2664366A
Cited
US2653917A
Cited
US2846407A
Cited
US3663470A
Cited
US3737398A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |