Method of producing low wear coating reinforced with brazing solder for use as rubbing seal
Assignee: Nissan Motor Co Ltd
•
Filing: 1976-08-10
•
Granted: 1978-06-13
•
Expires: 1996-08-10
Abstract
Abstract A low wear coating formed on a metal substrate to serve as a high temperature rubbing seal layer, comprising a surface layer made fundamentally of a wear resistant metal oxide such as nickel oxide and a solid lubricating material such as calcium fluoride and at least one intermediate layer made fundamentally of the metal oxide optionally with the addition of the lubricating material, wherein at least an outmost intermediate layer as well as an inmost region of the surface layer is impregnated with a brazing solder. The solder is added in the form of powder to the material of the intermediate layer prior to a flame spraying process and later caused to melt and permeate into the surface layer formed by flame spraying.
Inventors
- 👤 Katsuhiro Kishida
- 👤 Akira Oyamada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:30
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/18; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; C23C4/02; F; F16; F16J; F16J15/00; F16J15/16; F16J15/34; F16J15/3496; F28; F28D; F28D19/00; F28D19/04; F28D19/047
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
240 words
A method of producing a low wear coating useful as a high temperature rubbing contact seal layer on a metal substrate, the method comprising the steps of: forming at least one intermediate layer on said substrate by individually flame spraying a powdered material containing at least a major amount of a wear resistant metal oxide selected from the group consisting of NiO and CoO optionally with the addition of a minor amount of a solid lubricating material selected from the group consisting of MgF 2 , CaF 2 , BaF 2 , Mg 2 P 2 O 7 , Ca 2 P 2 O 7 , CaB 4 O 7 and PbO, said powdered material used for at least an outmost one of said at least one intermediate layer containing from 10 to 50 Wt% of a powder of a brazing solder selected from the group consisting of a nickel base solder, a copper base solder and a silver base solder; forming a surface layer on said outmost intermediate layer by flame spraying a powdered material consisting of a major amount of said metal oxide and a minor amount of said lubricating material; and thereafter heating said substrate with said at least one intermediate layer and said surface layer thereon to a temperature about the melting point of said brazing solder thereby to cause said brazing solder to melt and partially permeate into an inmost region of said surface layer.
Claim 2
Independent Claim
240 words
A method of producing a low wear coating useful as a high temperature rubbing contact seal layer on a metal substrate, the method comprising the steps of: forming at least one intermediate layer on said substrate by individually flame spraying a powdered material containing at least a major amount of a wear resistant metal oxide selected from the group consisting of NiO and CoO optionally with the addition of a minor amount of a solid lubricating material selected from the group consisting of MgF 2 , CaF 2 , BaF 2 , Mg 2 P 2 O 7 , Ca 2 P 2 O 7 , CaB 4 O 7 and PbO, said powdered material used for at least an outmost one of said at least one intermediate layer containing from 10 to 50 Wt% of a powder of a brazing solder selected from the group consisting of a nickel base solder, a copper base solder and a silver base solder; forming a surface layer on said outmost intermediate layer by flame spraying a powdered material consisting of a major amount of said metal oxide and a minor amount of said lubricating material; and thereafter heating said substrate with said at least one intermediate layer and said surface layer thereon to a temperature about the melting point of said brazing solder thereby to cause said brazing solder to melt and partially permeate into an inmost region of said surface layer.
Claim 3
Dependent Claim
16 words
A method as claimed in claim 1, wherein the heating step is carried out under vacuum.
Claim 4
Dependent Claim
15 words
A method as claimed in claim 1, wherein said brazing solder is a nickel-phosphorus solder.
Claim 5
Dependent Claim
34 words
A method as claimed in claim 1, further comprising the step of forming a bonding layer of an alloy on said substrate prior to the step of forming said at least one intermediate layer.
Claim 6
Dependent Claim
42 words
A method as claimed in claim 1, wherein at least two intermediate layers are formed at the firstly stated step, said powdered material for all of said at least two intermediate layers containing from 10 to 50 Wt% of said brazing solder.
Claim 7
Dependent Claim
40 words
A method as claimed in claim 1, wherein said surface layer is formed to have a larger thickness than any of said at least one intermediate layers, all said at least one intermediate layers being substantially of the same thickness.
Claim 8
Dependent Claim
48 words
A method as claimed in claim 6, wherein said temperature at the heating step is maintained for such a period of time that the thickness of said inmost region of said surface layer becomes from about 50 to about 100% of the thickness of said outmost intermediate layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-12 | 1981-12-12 | 1982-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-12 | 1985-12-12 | 1986-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-12 | 1989-12-12 | 1990-06-13 | $7700.00 | Window Closed / Lapsed |