US4092290A
Expired / Lapsed
US
⏱️ 0.0 years remaining
In situ curable sealant and methods for making and using same
Assignee: PPG Industries Inc
•
Filing: 1975-05-30
•
Granted: 1978-05-30
•
Expires: 1995-05-30
Abstract
Abstract A sealant suitable for use with multiple glazed window units is disclosed. The sealant comes in the form of two relatively low viscosity components, each of which has an unlimited storage life. When it is desired to apply the sealant, the components are fed to an extruder and blended together to form an initially uncured cold flowable mastic material of relatively low viscosity. Because each of the two components of the sealant composition is of low viscosity and the initially uncured composite of the two components blended together is also of low viscosity, the sealant can be extruded at relatively low temperatures, thus preventing premature rapid curing and insuring that the sealant composition will have a low viscosity and be cold-flowable immediately after extrusion. The sealant is then cured in situ at ambient temperature over a period of several weeks to form a firm, tacky, resilient seal.
Inventors
- 👤 George H. Bowser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:20
CPC Classifications
E; E06; E06B; E06B3/00; E06B3/66; E06B3/663; E06B3/66309; E06B3/66342; C; C08; C08K; C08K5/00; C08K5/16; C08K5/32; C08K5/33; C08L; C08L23/00; C08L23/02; C08L23/18; C08L23/20; C08L23/22; C09; C09J; C09J123/00; C09J123/02; C09J123/18; C09J123/20; C09J123/22; C08L2666/00; C08L2666/02; C08L2666/04; C08L2666/28; Y; Y10; Y10S; Y10S524/00; Y10S524/906
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
192 words
A room temperature vulcanizable sealant comprising an essentially solvent-free admixture of two rubbery components said admixture having an initial consistency of 100 to 300 metergrams and comprising: a. as a first component: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.2 to 2 percent by weight quinone dioxime; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; b. as a second component: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.4 to 5 percent by weight oxidizing agent; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; said polybutene being a copolymer of which 3 to 25 percent by weight is a butene-1, butene-2 moiety and 25 to 97 percent by weight is an isobutylene moiety and said admixture containing at least 3 percent by total weight of pigment or filler or a combination of pigment and filler.
Claim 2
Dependent Claim
192 words
A room temperature vulcanizable sealant comprising an essentially solvent-free admixture of two rubbery components said admixture having an initial consistency of 100 to 300 metergrams and comprising: a. as a first component: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.2 to 2 percent by weight quinone dioxime; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; b. as a second component: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.4 to 5 percent by weight oxidizing agent; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; said polybutene being a copolymer of which 3 to 25 percent by weight is a butene-1, butene-2 moiety and 25 to 97 percent by weight is an isobutylene moiety and said admixture containing at least 3 percent by total weight of pigment or filler or a combination of pigment and filler.
Claim 3
Dependent Claim
53 words
The sealant according to claim 1 wherein each component comprises: i. 18 to 35 percent by weight butyl rubber, ii. 8 to 20 percent by weight polyisobutylene, iii. 15 to 35 percent by weight polybutene, and iv. up to 40 percent of a pigment or filler or a combination of pigment and filler.
Claim 4
Dependent Claim
16 words
The sealant of claim 2 which contains up to 20 percent by weight of zirconium orthosilicate.
Claim 5
Dependent Claim
13 words
The sealant of claim 1 in which the oxidizing agent is lead oxide.
Claim 6
Dependent Claim
13 words
The sealant of claim 1 in which the quinone dioxime is paraquinone dioxime.
Claim 7
Dependent Claim
15 words
The sealant of claim 1 which contains up to 40 percent by weight carbon black.
Claim 8
Dependent Claim
15 words
The sealant of claim 1 which contains up to 30 percent by weight silica pigment.
Claim 9
Dependent Claim
15 words
The sealant of claim 1 which contains 1 to 10 percent by weight zinc oxide.
Claim 10
Dependent Claim
11 words
The sealant of claim 1 which further contains an organo silane.
Claim 11
Independent Claim
232 words
A method of making a room temperature vulcanizable sealant comprising the steps of: a. forming a first rubbery component which is essentially solvent-free and which comprises: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.2 to 2 percent by weight quinone dioxime; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; b. forming a second rubbery component which is essentially solvent-free and which comprises: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.4 to 5 percent by weight oxidizing agent; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; and c. extruding the compositions together at a temperature between about 120° F. and about 180° F. to form an initially uncured cold flowable mastic in bead or ribbon form which contains at least 3 percent by weight pigment or filler or a combination of pigment and filler and which has an initial consistency of 100 to 300 metergrams; said polybutene being a copolymer of about 3 to 25 percent by weight of a butene-1, butene-2 moiety and about 75 to 97 percent by weight of an isobutylene moiety.
Claim 12
Independent Claim
232 words
A method of making a room temperature vulcanizable sealant comprising the steps of: a. forming a first rubbery component which is essentially solvent-free and which comprises: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.2 to 2 percent by weight quinone dioxime; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; b. forming a second rubbery component which is essentially solvent-free and which comprises: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; iv. 0.4 to 5 percent by weight oxidizing agent; and v. at least 3 percent by weight pigment or filler or a combination of pigment and filler; and c. extruding the compositions together at a temperature between about 120° F. and about 180° F. to form an initially uncured cold flowable mastic in bead or ribbon form which contains at least 3 percent by weight pigment or filler or a combination of pigment and filler and which has an initial consistency of 100 to 300 metergrams; said polybutene being a copolymer of about 3 to 25 percent by weight of a butene-1, butene-2 moiety and about 75 to 97 percent by weight of an isobutylene moiety.
Claim 13
Dependent Claim
58 words
The method according to claim 10 wherein both the first and second compositions contain: i. 18 to 35 percent by weight butyl rubber, ii. 8 to 20 percent by weight polyisobutylene, iii. 15 to 35 percent by weight polybutene, and iv. up to 40 percent by weight of a pigment or filler or combination of pigment and filler.
Claim 14
Dependent Claim
22 words
The method as set forth in claim 11 in which the sealant contains up to 20 percent by weight of zirconium orthosilicate.
Claim 15
Dependent Claim
16 words
The method as set forth in claim 10 in which the oxidizing agent is lead oxide.
Claim 16
Dependent Claim
16 words
The method as set forth in claim 10 in which the quinone dioxime is paraquinone dioxime.
Claim 17
Dependent Claim
20 words
The method set forth in claim 10 in which the sealant contains up to 40 percent by weight carbon black.
Claim 18
Dependent Claim
21 words
The method as set forth in claim 10 in which the sealant contains up to 30 percent by weight silica pigment.
Claim 19
Dependent Claim
21 words
The method as set forth in claim 10 in which the sealant contains 1 to 10 percent by weight zinc oxide.
Claim 20
Dependent Claim
164 words
A room temperature vulcanizable sealant composition suitable for hermetically sealing multiple glazed window units comprising essentially: 18 to 35 percent by weight butyl rubber, 8 to 20 percent by weight polyisobutylene, 15 to 35 percent by weight polybutene, 0 to 40 percent by weight carbon black, 0 to 30 percent by weight silica pigment, 0 to 20 percent by weight zirconium orthosilicate, 1.0 to 10 percent by weight zinc oxide, the above percentages by weight based on the total weight of the sealant composition and 0.4 to 3.5 percent by weight of an oxidizing agent and 0.2 to 6 percent by weight of a quinone dioxime, the above percentages by weight based on the weight of butyl rubber, said sealant composition being essentially solvent-free and having initially a consistency of 100 to 300 metergrams; said polybutene being a copolymer of about 3 to 25 percent by weight of a butene-1, butene-2 moiety and about 75 to 97 percent by weight of an isobutylene moiety.
Claim 21
Dependent Claim
164 words
A room temperature vulcanizable sealant composition suitable for hermetically sealing multiple glazed window units comprising essentially: 18 to 35 percent by weight butyl rubber, 8 to 20 percent by weight polyisobutylene, 15 to 35 percent by weight polybutene, 0 to 40 percent by weight carbon black, 0 to 30 percent by weight silica pigment, 0 to 20 percent by weight zirconium orthosilicate, 1.0 to 10 percent by weight zinc oxide, the above percentages by weight based on the total weight of the sealant composition and 0.4 to 3.5 percent by weight of an oxidizing agent and 0.2 to 6 percent by weight of a quinone dioxime, the above percentages by weight based on the weight of butyl rubber, said sealant composition being essentially solvent-free and having initially a consistency of 100 to 300 metergrams; said polybutene being a copolymer of about 3 to 25 percent by weight of a butene-1, butene-2 moiety and about 75 to 97 percent by weight of an isobutylene moiety.
Claim 22
Dependent Claim
15 words
The sealant of claim 18 which contains up to 20 percent by weight zirconium orthosilicate.
Claim 23
Dependent Claim
15 words
The sealant of claim 18 which contains up to 40 percent by weight carbon black.
Claim 24
Dependent Claim
15 words
The sealant of claim 18 which contains up to 30 percent by weight silica pigment.
Claim 25
Dependent Claim
11 words
The sealant of claim 18 which further contains an organo silane.
Claim 26
Independent Claim
201 words
A method for sealing a structure which comprises the steps of: a. forming a room temperature vulcanizable sealant substantially free of hydrocarbon solvent comprising: i. 18 to 35 percent by weight butyl rubber, ii. 8 to 20 percent by weight polyisobutylene, iii. 15 to 35 percent by weight polybutene, iv. 0 to 40 percent by weight carbon black, v. 0 to 30 percent by weight silica pigment, vi. 0 to 20 percent by weight zirconium orthosilicate, vii. 1 to 10 percent by weight zinc oxide, the above percentages based on the total weight of the sealant composition and viii. 0.2 to 6 percent by weight of a quinone dioxime, and ix. 0.4 to 3.5 percent by weight of an oxidizing agent the above percentages based on the weight of butyl rubber, said sealant composition being initially essentially uncured and having an initial consistency of 100 to 300 metergrams; said polybutene being a copolymer of about 3 to 25 percent by weight of a butene-1, butene-2 moiety and about 75 to 97 percent by weight of an isobutylene moiety; b. applying said uncured sealant to the structure to be sealed; and c. allowing said sealant to cure in situ at ambient temperatures.
Claim 27
Independent Claim
201 words
A method for sealing a structure which comprises the steps of: a. forming a room temperature vulcanizable sealant substantially free of hydrocarbon solvent comprising: i. 18 to 35 percent by weight butyl rubber, ii. 8 to 20 percent by weight polyisobutylene, iii. 15 to 35 percent by weight polybutene, iv. 0 to 40 percent by weight carbon black, v. 0 to 30 percent by weight silica pigment, vi. 0 to 20 percent by weight zirconium orthosilicate, vii. 1 to 10 percent by weight zinc oxide, the above percentages based on the total weight of the sealant composition and viii. 0.2 to 6 percent by weight of a quinone dioxime, and ix. 0.4 to 3.5 percent by weight of an oxidizing agent the above percentages based on the weight of butyl rubber, said sealant composition being initially essentially uncured and having an initial consistency of 100 to 300 metergrams; said polybutene being a copolymer of about 3 to 25 percent by weight of a butene-1, butene-2 moiety and about 75 to 97 percent by weight of an isobutylene moiety; b. applying said uncured sealant to the structure to be sealed; and c. allowing said sealant to cure in situ at ambient temperatures.
Claim 28
Dependent Claim
112 words
The method according to claim 23 wherein the sealant is formed by extruding together at a temperature between about 120° F. and about 180° F: a. a first rubbery component comprising: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 25 percent by weight polybutene; and iv. 0.2 to 2 percent by weight of a quinone dioxime; and b. a second rubbery component comprising: i. 18 to 35 percent by weight butyl rubber; ii. 8 to 20 percent by weight polyisobutylene; iii. 15 to 35 percent by weight polybutene; and iv. 0.4 to 5 percent by weight of an oxidizing agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |