Production of water-dispersible polyurethanes having ionic groups and hydrophilic side chains
Assignee: Bayer AG
•
Filing: 1976-11-15
•
Granted: 1978-05-30
•
Expires: 1996-11-15
Abstract
Abstract The present invention relates to water-dispersible polyurethane elastomers having a substantially linear molecular structure, characterized by (a) lateral polyalkylene oxide polyether chains having a content of ethylene oxide units of from about 0.5 to 10% by weight, based on the polyurethane as a whole and (b) a content of ═N⊕═, --COO⊖ or --SO 3 ⊖ groups of from about 0.1 to 15 milliequivalents per 100 g, To aqueous dispersions of these water-dispersible polyurethane elastomers and to processes for producing these water-dispersible polyurethane elastomers.
Inventors
- 👤 Klaus Noll
- 👤 Jurgen Grammel
- 👤 Walter Meckel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:22
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0804; C08G18/28; C08G18/40; C08G18/48; C08G18/50; C08G18/5021; C08G18/5036; C08G18/5042; Y; Y10; Y10S; Y10S260/00; Y10S260/15; Y10S260/17; Y10S260/18
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
65 words
Water-dispersible polyurethanes having a substantially linear molecular structure, characterized by: (a) lateral polyalkylene oxide polyether chains having a content of laterally incorporated ethylene oxide units sufficient to provided from about 0.5 to 10%, of the weight of the polyurethane as a whole, and, (b) a content of ═N.sup.⊕ ═, --COO.sup.⊖ or --SO 3 .sup.⊖ groups of from about 0.1 to 15 milliequivalents per 100 g.
Claim 2
Dependent Claim
65 words
Water-dispersible polyurethanes having a substantially linear molecular structure, characterized by: (a) lateral polyalkylene oxide polyether chains having a content of laterally incorporated ethylene oxide units sufficient to provided from about 0.5 to 10%, of the weight of the polyurethane as a whole, and, (b) a content of ═N.sup.⊕ ═, --COO.sup.⊖ or --SO 3 .sup.⊖ groups of from about 0.1 to 15 milliequivalents per 100 g.
Claim 3
Dependent Claim
9 words
Aqueous dispersions of the polyurethanes claimed in claim 1.
Claim 4
Dependent Claim
49 words
The water-dispersible polyurethanes of claim 1 wherein the content of laterally incorporated ethylene oxide units is sufficient to provide from about 1.5 to 6% of the weight of the polyurethane as a whole, and the content of ionic groups is from about 0.4 to 12 milliequivalents per 100 g.
Claim 5
Dependent Claim
41 words
The water dispersible polyurethane of claim 1 wherein the content of milliequivalents of ionic groups per 100 g of polyurethane plus the number of psuedo-milliequivalents of lateral ethylene oxide units per 100 g of polyurethane is from about 5 to 30.
Claim 6
Dependent Claim
110 words
A process for the production of a water-dispersible polyurethane having a substantially linear molecular structure comprising reacting (a) organic diisocyanates, (b) organic difunctional compounds having isocyanatereactive end groups and having a molecular weight of from about 300 to 6000, and (c) synthesis components containing hydrophilic groups or groups convertible into hydrophilic groups, said groups responsible for the dispersibility of the polyurethane, so as to produce a polyurethane which contains from about 0.5 to 10% by weight of lateral ethylene oxide units, and from about 0.1 to 0.1 to 15 milliequivalents of ionic groups selected from the group consisting ═N.sup.⊕ ═, --COO.sup.⊖ and --SO 3 .sup.⊖ per 100 g of polyurethane.
Claim 7
Dependent Claim
110 words
A process for the production of a water-dispersible polyurethane having a substantially linear molecular structure comprising reacting (a) organic diisocyanates, (b) organic difunctional compounds having isocyanatereactive end groups and having a molecular weight of from about 300 to 6000, and (c) synthesis components containing hydrophilic groups or groups convertible into hydrophilic groups, said groups responsible for the dispersibility of the polyurethane, so as to produce a polyurethane which contains from about 0.5 to 10% by weight of lateral ethylene oxide units, and from about 0.1 to 0.1 to 15 milliequivalents of ionic groups selected from the group consisting ═N.sup.⊕ ═, --COO.sup.⊖ and --SO 3 .sup.⊖ per 100 g of polyurethane.
Claim 8
Dependent Claim
76 words
The process of claim 5 wherein the synthesis components containing hydrophilic groups or groups convertible into hydrophilic groups are (i) compounds having hydrophilic side chains containing ethylene oxide units selected from the group consisting of diisocyanates and difunctional compounds having isocyanate-reactive hydrogen atoms, and (ii) compounds having ionic groups or groups convertible into ionic groups selected from the group consisting of monoisocyanates, diisocyanates, monofunctional compounds having isocyanate-reactive hydrogen atoms, and difunctional compounds having isocyanate-reactive hydrogen atoms.
Claim 9
Dependent Claim
140 words
The process of claim 6 wherein the component (i) hydrophilic component is selected from the group consisting of diols of the formula ##STR5## and the diisocyanates of the formula ##STR6## wherein: R represents a difunctional radical of the type obtained by removing the isocyanate groups from a diisocyanate having a molecular weight of from about 112 to 1000, R' represents hydrogen or a monofunctional hydrocarbon radical having from 1 to 8 carbon atoms, X represents a difunctional radical obtained by removing the terminal oxygen atom from a polyalkylene oxide radical having from about 5 to 90 chain members of which at least about 40% consist of ethylene oxide units, Y and Z represents oxygen or --NR"'--, and R" and R"', which may be the same or different, each represents a monofunctional hydrocarbon radical having from 1 to 12 carbon atoms.
Claim 10
Dependent Claim
66 words
The process of claim 7 wherein X represents a difunctional radical obtained by removing the terminal oxygen atom from a polyalkylene oxide radical having from about 5 to 90 chain members of which at least about 40% consist of ethylene oxide units and of which the remainder consists of alkylene oxide units selected from the group consisting of propylene oxide, butylene oxide and styrene oxide units.
Claim 11
Dependent Claim
63 words
The process of claim 6 wherein the component (ii) hydrophilic component is selected from the group consisting of aliphatic diols containing sulphonate groups and diamino sulphonates corresponding to the formula H.sub.2 N--A--NH--B--SO.sub.3.sup.⊖ Kat.sup.⊕ wherein A and B represent aliphatic hydrocarbon radicals having from 2 to 6 carbon atoms, and Kat.sup.⊕ represents an optionally substituted ammonium cation, a sodium cation or a potassium cation.
Claim 12
Dependent Claim
32 words
The process of claim 5 wherein the groups convertible into hydrophilic groups are at least partially converted into hydrophilic groups during or after the polyaddition reaction between components (a), (b) and (c).
Claim 13
Dependent Claim
17 words
The process of claim 5 wherein chain extenders having a molecular weight below about 300 are used.
Claim 14
Dependent Claim
26 words
The process of claim 5 wherein the reactants are used in an equivalent ratio of isocyanate groups to isocyanate-reactive groups of from about 0.8:1 to 2.5:1.
Claim 15
Dependent Claim
32 words
The process of claim 5 wherein the organic difunctional compounds having isocyanate-reactive end groups are selected from the group of compounds consisting of dihydroxy polyesters, dihydroxy polyactones, dihydroxy polyethers and dihydroxy polycarbonates.
Claim 16
Dependent Claim
19 words
The aqueous dispersions of claim 2 wherein the average particle size is from about 10 mμ to 5 μ.
Claim 17
Dependent Claim
35 words
The process of claim 7 wherein the component (i) hydrophilic component is a diol corresponding to the formula ##STR7## wherein R, R', X, Y, R" and R"' have the same meaning as in claim 10.
Claim 18
Dependent Claim
42 words
The process of claim 6 wherein the component (ii) hydrophilic component is selected from the group consisting of diols containing sulfonate groups and aliphatically bound hydroxyl groups, diamines containing aliphatically bound primary amino groups and diamines containing aliphatically bound secondary amino groups.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |