Method of forming a metallic thin film by electroless plating on a vinylidene chloride undercoat
Assignee: Fujifilm Holdings Corp
•
Filing: 1976-10-19
•
Granted: 1978-05-16
•
Expires: 1996-10-19
Abstract
Abstract This invention relates to a method of forming a metallic thin film on a plastic substrate by electroless plating, which comprises providing an undercoated layer consisting essentially of polyvinylidene chloride or vinylidene chloride copolymer on the surface of the plastic substrate and then subjecting to a surface activating treatment and electroless plating.
Inventors
- 👤 Ryuji Shirahata
- 👤 Masaaki Suzuki
- 👤 Yasuyuki Yamada
- 👤 Tatsuji Kitamoto
- 👤 Shin-ichiro Dezawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 01:46
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28; C23C18/30; C23C18/2006; C23C18/2026; C23C18/2033; C23C18/2046; C23C18/2053; C23C18/2066; C23C18/2073; C23C18/208; C23C18/22; C23C18/24; C23C18/285; H; H05; H05K; H05K3/00; H05K3/38; H05K3/386; H05K3/387
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
198 words
A method of forming a metallic thin film on a plastic substrate by electroless plating which consists essentially of (a) providing on a surface of the substrate an undercoated layer of a vinylidene chloride copolymer selected from the group consisting of vinylidene chloride-vinyl chloride copolymers and vinylidene chloride-acrylonitrile copolymers, the vinylidene chloride copolymer having a softening point of 100° to 200° C and a degree of polymerization of at most 1000 and having a vinylidene chloride content of 8 to 98% by weight, (b) subjecting the surface of the layer to surface activating treatment of (1) sensitizing the surface with a sensitizer solution containing hydrochloric acid and stannous chloride followed by activation with an activator containing a noble metal ion, or (2) contacting the surface with a catalyst containing stannous and noble metal ions followed by contacting the surface with an accelerator, and (c) subjecting the resulting surface to electroless plating in an electroless plating bath containing 0.02 to 0.6 mol/l of cobalt ion, 0 to 0.02 mol/l of nickel ion and 0.03 to 0.4 mol/l of hypophosphite ion, optionally with a complexing agent, pH buffering agent and pH regulator, whereby metal ions are deposited on the surface.
Claim 2
Independent Claim
198 words
A method of forming a metallic thin film on a plastic substrate by electroless plating which consists essentially of (a) providing on a surface of the substrate an undercoated layer of a vinylidene chloride copolymer selected from the group consisting of vinylidene chloride-vinyl chloride copolymers and vinylidene chloride-acrylonitrile copolymers, the vinylidene chloride copolymer having a softening point of 100° to 200° C and a degree of polymerization of at most 1000 and having a vinylidene chloride content of 8 to 98% by weight, (b) subjecting the surface of the layer to surface activating treatment of (1) sensitizing the surface with a sensitizer solution containing hydrochloric acid and stannous chloride followed by activation with an activator containing a noble metal ion, or (2) contacting the surface with a catalyst containing stannous and noble metal ions followed by contacting the surface with an accelerator, and (c) subjecting the resulting surface to electroless plating in an electroless plating bath containing 0.02 to 0.6 mol/l of cobalt ion, 0 to 0.02 mol/l of nickel ion and 0.03 to 0.4 mol/l of hypophosphite ion, optionally with a complexing agent, pH buffering agent and pH regulator, whereby metal ions are deposited on the surface.
Claim 3
Dependent Claim
37 words
The method of claim 1, wherein the sensitizer contains 0.16-150 g/l of stannous chloride and 0.8-200 m/l of hydrochloric acid and the activator contains 0.0001-0.012 mol/l of a noble metal ion and 3-20 ml/l of hydrochloric acid.
Claim 4
Dependent Claim
67 words
The method of claim 1, wherein the catalyst contains 0.01-0.98 mol/l of stannous ion, 0-0.02 mol/l of stannic ion, 0.0001-0.012 mol/l of a noble metal ion and 0.5-350 ml/l of hydrochloric acid and the accelerator contains 5-50% of at least one member selected from the group consisting of perchloric acid, sulfuric acid, phosphoric acid, sodium hydroxide, sodium carbonate, sodium pyrophosphate, ammonium fluoride, hydrofluoric acid and mixtures thereof.
Claim 5
Dependent Claim
20 words
The method of claim 1, wherein the vinylidene chloride copolymer contains 95 to 18% by weight of vinylidene chloride component.
Claim 6
Dependent Claim
28 words
The method of claim 1, wherein the undercoated layer contains, in addition, at most 50% by weight of additives based on the polyvinylidene chloride or vinylidene chloride copolymer.
Claim 7
Dependent Claim
25 words
The method of claim 5, wherein the additives is selected from the group consisting of plasticizers, heat stabilizers and adhesion improving agents to plastic substrates.
Claim 8
Dependent Claim
17 words
The method of claim 1, wherein the undercoated layer has a thickness of 0.2 to 2 μm.
Claim 9
Dependent Claim
16 words
The method of claim 1, wherein the plastic substrate is of polyethylene terephthalate or polyethylene naphthalate.
Claim 10
Dependent Claim
16 words
The method of claim 1, wherein a magnetic thin film is formed by the electroless plating.
Claim 11
Dependent Claim
16 words
The method of claim 9, wherein the magnetic thin film consists essentially of cobalt of cobalt-nickel.
Claim 12
Dependent Claim
18 words
The method of claim 9, wherein the magnetic thin film has a thickness of 0.05 to 2.0 μm.
Claim 13
Dependent Claim
18 words
The method of claim 1, wherein the undercoated layer has a surface roughness of at most 0.5 μm.
References Cited (Backward Citations)
GB861710A
Cited
US3011920A
Cited
US3238061A
Cited
US3698929A
Cited
FR2071494A5
Cited
US4005238A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-15 | 1981-11-14 | 1982-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-15 | 1985-11-14 | 1986-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-15 | 1989-11-14 | 1990-05-16 | $7700.00 | Window Closed / Lapsed |