Melt processable thermotropic wholly aromatic polyester containing polybenzoyl units
Assignee: Celanese Corp
•
Filing: 1976-05-13
•
Granted: 1978-01-10
•
Expires: 1996-05-13
Abstract
Abstract A wholly aromatic polyester is provided which unlike the aromatic polyesters normally encountered in the prior art is not intractable or difficultly tractable and readily undergoes melt processing with ease. The aromatic polyester of the present invention consists essentially of the recurring units (a) p-oxybenzoyl moiety , (b) 2,5-dicarboxynaphthalene moiety, and (c) symmetrical dioxy aryl moiety (as defined), and is free of units which possess ring substitution. The resulting polyester exhibits a melting point below approximately 425° C., preferably below 350° C., and most preferably below approximately 330° C. The ability of the wholly aromatic polyester to readily undergo melt processing can be attributed to its atypical inherent propensity to form a thermotropic melt phase which is exhibited in the absence of ring substitution. The particularly effective route for forming the wholly aromatic polyester is via a slurry polymerization technique (as defined).
Inventors
- 👤 Gordon W. Calundann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 10:29
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; C08G63/60; C08G63/605
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
54 words
An improved melt processable wholly aromatic polyester capable of forming a thermoplastic melt phase at a temperature below approximately 350° C. consisting essentially of the recurring moieties I, II and III wherein: I is ##STR14##II is ##STR15## and III is ##STR16##and wherein said polyester comprises approximately 35 to 80 mole percent of moiety I.
Claim 2
Dependent Claim
54 words
An improved melt processable wholly aromatic polyester capable of forming a thermoplastic melt phase at a temperature below approximately 350° C. consisting essentially of the recurring moieties I, II and III wherein: I is ##STR14##II is ##STR15## and III is ##STR16##and wherein said polyester comprises approximately 35 to 80 mole percent of moiety I.
Claim 3
Dependent Claim
53 words
An improved melt processable wholly aromatic polyester capable of forming a thermotropic melt phase at a temperature below approximately 350° C. consisting of the recurring moieties I, II, and III wherein: I is ##STR17##II is ##STR18## and III is ##STR19##and wherein said polyester comprises approximately 40 to 75 mole percent of moiety I.
Claim 4
Dependent Claim
53 words
An improved melt processable wholly aromatic polyester capable of forming a thermotropic melt phase at a temperature below approximately 350° C. consisting of the recurring moieties I, II, and III wherein: I is ##STR17##II is ##STR18## and III is ##STR19##and wherein said polyester comprises approximately 40 to 75 mole percent of moiety I.
Claim 5
Dependent Claim
35 words
A melt processble wholly aromatic polyester according to claim 2 which is capable of forming a thermotropic melt phase below approximately 330° C. and which comprises approximately 50 to 70 mole percent of moiety I.
Claim 6
Dependent Claim
22 words
A melt processable wholly aromatic polyester according to claim 2 wherein the molar quantities of moieties II and III are substantially equal.
Claim 7
Dependent Claim
35 words
A melt processable wholly aromatic polyester according to claim 2 which consists of approximately 60 mole percent of moiety I, approximately 20 mole percent of moiety II, and approximately 20 mole percent of moiety III.
Claim 8
Dependent Claim
31 words
An improved molding compound comprising the melt processable wholly aromatic polyester of claim 2 which incorporates therein about 1 to 60 percent by weight of a solid filler and/or reinforcing agent.
Claim 9
Dependent Claim
23 words
A melt processable wholly aromatic polyester according to claim 1 which is capable of forming a thermotropic melt phase below approximately 330° C.
Claim 10
Dependent Claim
20 words
A melt processable wholly aromatic polyester according to claim 7 which comprises 40 to 75 mole percent of moiety I.
Claim 11
Dependent Claim
22 words
A melt processable wholly aromatic polyester according to claim 1 wherein the molar quantities of moieties II and III are substantially equal.
Claim 12
Dependent Claim
40 words
A melt processable wholly aromatic polyester according to claim 1 which comprises approximately 35 to 80 mole percent of moiety I, approximately 7.5 to 32.5 mole percent of moiety II, and approximately 7.5 to 32.5 mole percent of moiety III.
Claim 13
Dependent Claim
31 words
An improved molding compound comprising the melt processable wholly aromtic polyester of claim 1 which incorporates therein about 1 to 60 percent by weight of a solid filler and/or reinforcing agent.
References Cited (Backward Citations)
US3637595A
Cited
US3890256A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |