US4066821A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Tungsten carbide tools treated with group IVB and VB metals
Assignee: Massachusetts Institute of Technology
•
Filing: 1976-01-22
•
Granted: 1978-01-03
•
Expires: 1996-01-22
Abstract
Abstract Tungsten carbide tools are provided having improved wear properties which tools produce an improved surface finish on workpieces cut with said tools, both initially and after extended use. The tools are prepared by a process which comprises applying a coating of a Group IVB or VB metal of the Periodic Chart of the Elements over the tool, diffusing said metal into the tool and removing any excess of the metal from the surface of the tool, possibly by further diffusion of the metal into the tool. The preferred method is by gaseous decomposition of a metal halide in an atmosphere which does not contain a carbon source such as methane, used in some previous processes. The source of the carbon in the Group IVB or VB metal carbide is the carbon in the carbide tool being coated. Tools formed in accordance with the invention have wear properties such that they typically last at least four times as long as untreated tools and under most preferred conditions, as much as nine times as long as untreated tools.
Inventors
- 👤 Nathan Henry Cook
- 👤 Bruce M. Kramer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 06:28
CPC Classifications
C; C23; C23C; C23C30/00; C23C30/005; B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; B23P; B23P15/00; B23P15/28; C22; C22C; C22C29/00
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
103 words
A method for forming a coating of a Group IVB or VB metal carbide on a carbide tool, said method comprising the steps of applying a Group IVB or VB metal to the surface of said tool by vapor deposition in an atmosphere which consists essentially of a halide of the Group IVB or VB metal and elemental halogen, and diffusing said metal into said tool at a temperature which is sufficient to permit formation of the Group IVB or VB metal carbide, the source of the carbon in said Group IVB or VB metal carbide being the carbon in said carbide tool.
Claim 2
Independent Claim
103 words
A method for forming a coating of a Group IVB or VB metal carbide on a carbide tool, said method comprising the steps of applying a Group IVB or VB metal to the surface of said tool by vapor deposition in an atmosphere which consists essentially of a halide of the Group IVB or VB metal and elemental halogen, and diffusing said metal into said tool at a temperature which is sufficient to permit formation of the Group IVB or VB metal carbide, the source of the carbon in said Group IVB or VB metal carbide being the carbon in said carbide tool.
Claim 3
Dependent Claim
14 words
The method of claim 1 where the metal is of a Group IVB metal.
Claim 4
Dependent Claim
10 words
The method of claim 2 where the metal is titanium.
Claim 5
Dependent Claim
10 words
The method of claim 1 where the metal is hafnium.
Claim 6
Dependent Claim
13 words
The method of claim 1 where the metal is a Group VB metal.
Claim 7
Dependent Claim
14 words
The method of claim 1 wherein the carbide tool is a tungsten carbide tool.
Claim 8
Dependent Claim
13 words
The method of claim 6 where the metal is a Group IVB metal.
Claim 9
Dependent Claim
10 words
The method of claim 6 wherein the metal is titanium.
Claim 10
Dependent Claim
10 words
The method of claim 6 wherein the metal is hafnium.
Claim 11
Dependent Claim
13 words
The method of claim 6 wherein the metal is a Group VB metal.
Claim 12
Dependent Claim
12 words
A hafnium carbide coated tool made by the process of claim 4.
Claim 13
Dependent Claim
19 words
The method of claim 1 where the metal is applied to the tool and simultaneously diffused into said tool.
Claim 14
Dependent Claim
19 words
The method of claim 1 where the metal is diffused into the tool subsequent to application to the tool.
Claim 15
Dependent Claim
45 words
The method of claim 12 where the temperature and time relationship for applying the metal to the surface of the tool and for diffusing said metal onto the tool are sufficient to diffuse the metal at least 2 μm into the surface of the tool.
Claim 16
Dependent Claim
47 words
The method of claim 12 where the temperature and time relationship for applying the metal to the surface of the tool and for diffusing said metal into the tool are sufficient to diffuse the metal from 5 μm to 2 μm into the surface of the tool.
Claim 17
Dependent Claim
13 words
The method of claim 12 where the temperature is at least 1500° F.
Claim 18
Dependent Claim
15 words
The method of claim 16 where the temperature varies between 1500° F and 3000° F.
Claim 19
Dependent Claim
15 words
The method of claim 16 where the temperature varies between 1525° F and 2250° F.
Claim 20
Dependent Claim
13 words
The method of claim 16 where the time is at least one minute.
Claim 21
Dependent Claim
14 words
The method of claim 16 where the time varies between 1/2 and 10 hours.
Claim 22
Dependent Claim
14 words
The method of claim 20 where the time varies between 2 and 4 hours.
Claim 23
Dependent Claim
26 words
The method of claim 1, further comprising removing Group IVB or VB metal that has not diffused into said tool from the surface of said tool.
Claim 24
Dependent Claim
16 words
The method of claim 22 where the metal is removed by diffusing it into the tool.
Claim 25
Dependent Claim
14 words
The method of claim 22 where the metal is removed with an acid dip.
Claim 26
Dependent Claim
14 words
The method of claim 22 where the metal is removed with a caustic dip.
Claim 27
Dependent Claim
20 words
The method of claim 1 wherein a layer of Group IVB or VB metal is deposited in free metal form.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-02 | 1981-07-04 | 1982-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-02 | 1985-07-04 | 1986-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-02 | 1989-07-04 | 1990-01-03 | $7700.00 | Window Closed / Lapsed |