Water soluble wire enamels

Claim 2

A water soluble wire enamel having a Class F thermal rating which is the reaction product of the ingredients comprising: a. from 45 to 55 weight percent of a water soluble polyester resin which is the reaction product of the ingredients comprising from 25 to 35 weight percent terephthalic acid, from 5 to 15 weight percent trimellitic anhydride, from 10 to 15 weight percent adipic acid, from 25 to 35 weight percent neopentyl glycol, and from 5 to 10 weight percent tris 2-hydroxyethyl isocyanurate, said polyester resin being in the form of a 60 to 80 weight percent solution in an ether glycol; b. from 3 to 5 weight percent of an ethanol-substituted amine; c. from 35 to 50 weight percent water; and d. from 1 to 2.5 weight percent of a triethanolamine titanate crosslinking agent.

Claim 3

The water soluble wire enamel of claim 1 wherein the polyester resin ingredients further comprise from 3 to 8 weight percent propylene glycol.

Claim 4

The water soluble wire enamel of claim 1 wherein the ether glycol is diethylene glycol.

Claim 5

The water soluble wire enamel of claim 1 wherein the ethanol-substituted amine is dimethylethanol amine.

Claim 6

A water soluble wire enamel having a Class F thermal rating which is the reaction product of the ingredients comprising: a. about 52.3 weight percent of a water soluble polyester resin which is the reaction product of the ingredients comprising about 30.9 weight percent terephthalic acid, 10.7 weight percent trimellitic anhydride, 13.6 weight percent adipic acid, 32.1 weight percent neopentyl glycol, 4.9 weight percent propylene glycol, and 7.8 weight percent tris 2-hydroxyethyl isocyanurate, said polyester resin ingredient being diluted to a 69 weight percent solution in diethylene glycol; b. about 3.7 weight percent dimethylethanol amine; c. about 41.8 weight percent water; and d. about 1.8 weight percent of an 80 weight percent solution of triethanolamine titanate in isopropanol.

Claim 7

A water soluble wire enamel having a Class F thermal rating which is the reaction product of the ingredients comprising: a. about 52.3 weight percent of a water soluble polyester resin which is the reaction product of the ingredients comprising about 30.9 weight percent terephthalic acid, 10.7 weight percent trimellitic anhydride, 13.6 weight percent adipic acid, 32.1 weight percent neopentyl glycol, 4.9 weight percent propylene glycol, and 7.8 weight percent tris 2-hydroxyethyl isocyanurate, said polyester resin ingredient being diluted to a 69 weight percent solution in diethylene glycol; b. about 3.7 weight percent dimethylethanol amine; c. about 41.8 weight percent water; and d. about 1.8 weight percent of an 80 weight percent solution of triethanolamine titanate in isopropanol.