Spray casting of gas atomized molten metal to produce high density ingots

Claim 2

A process for producing a spray cast metal ingot characterized by high density in the as-spray cast condition of substantially over 90% of the actual density of the metal which comprises, providing a highly energetic conically configurated outwardly expanding atomized metal stream having an included angle of substantially less than 25°, directing said atomized stream of metal to the interior of an ingot mold with the longitudinal axis of said stream disposed at an acute angle to the interior wall of said mold, while effecting relative transverse movement between said atomized metal stream and said mold, such that said stream is caused to scan the interior of said mold, and filling said mold while scanning the interior thereof.

Claim 3

The process of claim 1, wherein said highly energetic atomized metal stream is produced by impinging a teeming metal stream with an atomizing fluid flowing at supersonic velocity and coaxially in the direction of said teeming metal stream.

Claim 4

The process of claim 2, wherein the included angle of said conically configurated metal stream does not exceed about 20°.

Claim 5

The process of claim 3, wherein said included angle ranges from about 5° to 15°.

Claim 6

The process of claim 4, wherein said included angle ranges from about 5° to 10°.

Claim 7

The process of claim 2, wherein the temperature of the atomized metal ranges from about 85% of its absolute melting point to about its melting point.

Claim 8

The process of claim 2, wherein the axis of said metal stream is disposed at an acute angle to the interior wall of said mold of about 5° to 45°.

Claim 9

A process for producing a spray cast metal ingot characterized by high density in the as-spray cast condition of substantially over 90% of the actual density of the metal which comprises, providing a highly energetic conically configurated outwardly expanding atomized metal stream produced by impinging a teeming metal stream with a non-oxidizing atomizing gas flowing at supersonic velocity and coaxially in the direction of said teeming metal stream such that the resulting atomized metal stream has an included angle of substantially less than 25°, directing said atomized stream of metal to the interior of an ingot mold with the longitudinal axis of said stream disposed at an acute angle to the interior wall of said mold, while effecting relative transverse movement between said atomized metal stream and said mold, such that said stream is caused to scan the interior of said mold, and filling said mold while scanning the interior thereof.

Claim 10

A process for producing a spray cast metal ingot characterized by high density in the as-spray cast condition of substantially over 90% of the actual density of the metal which comprises, providing a highly energetic conically configurated outwardly expanding atomized metal stream produced by impinging a teeming metal stream with a non-oxidizing atomizing gas flowing at supersonic velocity and coaxially in the direction of said teeming metal stream such that the resulting atomized metal stream has an included angle of substantially less than 25°, directing said atomized stream of metal to the interior of an ingot mold with the longitudinal axis of said stream disposed at an acute angle to the interior wall of said mold, while effecting relative transverse movement between said atomized metal stream and said mold, such that said stream is caused to scan the interior of said mold, and filling said mold while scanning the interior thereof.

Claim 11

The process of claim 8, wherein the included angle of said conically configurated metal stream does not exceed about 20°.

Claim 12

The process of claim 9, wherein said included angle ranges from about 5° to 15°.

Claim 13

The process of claim 10, wherein said included angle ranges from about 5° to 10°.

Claim 14

The process of claim 8, wherein the temperature of the atomized metal ranges from about 85% of its absolute melting point to about its melting point.

Claim 15

The process of claim 8, wherein the axis of said metal stream is disposed at an acute angle to the inner surface of the wall of said mold of about 5° to 25°.

Claim 16

A process for producing a spray cast metal ingot characterized by high density of substantially over 90% of the actual density of the metal which comprises: providing a teeming stream of molten metal under substantially non-oxidizing conditions, allowing said molten metal stream to pass longitudinally and centrally though a hollow converging conical jet stream of super cooled non-oxidizing atomizing gas flowing at supersonic velocity downwardly and coaxially of said molten metal stream, the conical gas stream being focused at said supersonic velocity to impinge substantially symmetrically against said coaxially disposed molten metal stream in the direction of flow thereof and at a conical angle of impingement of less than 30° to produce a highly energetic outwardly expanding conically configurated atomized stream of molten metal with an included angle of substantially less than 25°, directing said conically configurated atomized stream of metal into the interior of an ingot mold supported transverse to the path of said energetic metal stream with the longitudinal axis of said metal stream disposed at an acute angle to the interior wall of said mold, causing said atomized stream of metal to scan the interior of said mold and strike the wall thereof at an acute angle by effecting relative transverse movement between said atomized metal stream and said mold to promote substantially uniform filling thereof, and continuing the filling of said mold with the axis of said atomized metal stream directed at said acute angle to the interior wall of said mold until the mold has been filled, thereby obtaining a compact high density spray cast ingot having an average density of substantially over 90% of the actual density of said metal.

Claim 17

A process for producing a spray cast metal ingot characterized by high density of substantially over 90% of the actual density of the metal which comprises: providing a teeming stream of molten metal under substantially non-oxidizing conditions, allowing said molten metal stream to pass longitudinally and centrally though a hollow converging conical jet stream of super cooled non-oxidizing atomizing gas flowing at supersonic velocity downwardly and coaxially of said molten metal stream, the conical gas stream being focused at said supersonic velocity to impinge substantially symmetrically against said coaxially disposed molten metal stream in the direction of flow thereof and at a conical angle of impingement of less than 30° to produce a highly energetic outwardly expanding conically configurated atomized stream of molten metal with an included angle of substantially less than 25°, directing said conically configurated atomized stream of metal into the interior of an ingot mold supported transverse to the path of said energetic metal stream with the longitudinal axis of said metal stream disposed at an acute angle to the interior wall of said mold, causing said atomized stream of metal to scan the interior of said mold and strike the wall thereof at an acute angle by effecting relative transverse movement between said atomized metal stream and said mold to promote substantially uniform filling thereof, and continuing the filling of said mold with the axis of said atomized metal stream directed at said acute angle to the interior wall of said mold until the mold has been filled, thereby obtaining a compact high density spray cast ingot having an average density of substantially over 90% of the actual density of said metal.

Claim 18

The process of claim 14, wherein said mold is moved relative to said atomized metal stream by rotation about its axis and by oscillating said mold across said stream of atomized metal.

Claim 19

The process of claim 14, wherein said jet stream of atomizing gas is produced by a plurality of jets substantially equally spaced in a circle and projecting downwardly at an angle to produce said conical angle of impingement of less than about 30° and wherein the axis of the metal stream is disposed at an acute angle to the interior wall of said mold of about 5° to 25°.

Claim 20

The process of claim 16, wherein said plurality of jets is arranged to provide following impingement of said atomizing gas a highly energetic tight cone of atomized metal having an included angle not exceeding about 20°.

Claim 21

The process of claim 17, wherein the plurality of jets is arranged to provide a tight cone of highly energetic stream of atomized metal having an included angle of about 5° to 15°.

Claim 22

The process of claim 18, wherein said tight cone of said highly energetic stream of atomized metal has an included angle of about 5° to 10°.

Claim 23

The process of claim 17, wherein the temperature of the atomized metal stream reaching the mold ranges from about 85% of the absolute melting point of the metal to its absolute melting point.

Claim 24

The process of claim 14, wherein the exit velocity of the atomizing gas leaving the jets is at least about Mach No. 1.5.

Claim 25

The process of claim 21, wherein the exit velocity of the atomizing gas leaving the jets is at least about Mach No. 2.

Claim 26

The process of claim 14, wherein the atomizing gas is argon.

Claim 27

The process of claim 14, wherein the teeming rate of the metal stream ranges from about 10 to 70 kg/min.

Claim 28

The process of claim 17, wherein the teeming rate of the metal stream ranges from about 25 to 50 kg/min.

Claim 29

The process of claim 24, wherein the nozzle through which the molten metal is teemed ranges in throat diameter from about 0.2 inch and up to about 0.375 inch.

Claim 30

The process of claim 17, wherein the gas is argon, the teeming rate of the molten metal through the nozzle ranges from about 10 to 70 kg/min., the throat diameter of the nozzle from about 0.2 inch to about 0.375 inch and the kinetic energy generated at the exits of the jets is correlated with the argon driving pressure and jet throat diameter as set forth in FIG. 7.

Claim 31

The process of claim 14, wherein said jet stream of atomizing gas is produced by a plurality of jets substantially equally spaced in a circle with a first set of alternate jets projecting downwardly to define an included conical angle of impingement of less than about 30° and a second set of alternate jets projecting downwardly to define an included conical angle of at least 2° less than the angle formed by said first set, thereby providing a double impact mode system on said teeming molten metal stream in which the impingement produced by said second set of alternate jets is below the impingement produced by said first set of jets, such that by virtue of said double mode impact, a relatively tight cone of atomized metal is produced having an included angle of substantially less than 25° C.

Claim 32

The process of claim 28, wherein said mold is moved relative to said atomized metal stream by rotation about its axis and by oscillating said mold across said stream of atomized metal.

Claim 33

The process of claim 28, wherein the arrangement of said first and second jets is such as to produce a highly energetic tight cone of atomized metal having an included angle not exceeding 20°.

Claim 34

The process of claim 30, wherein the arrangement of said first and second jets is such as to provide a tight cone of highly energetic stream of atomized metal having an included angle of about 5° to 15°.

Claim 35

The process of claim 31, wherein said tight cone of atomized metal has an included angle of about 5° to 10°.

Claim 36

The process of claim 28, wherein the temperature of the atomized metal stream reaching the mold ranges from about 85% of the absolute melting point of the metal to its absolute melting point.

Claim 37

The process of claim 28, wherein the exit velocity of the atomizing gas leaving the jets is at least about Mach No. 1.5.

Claim 38

The process of claim 34, wherein the exit velocity of the atomizing gas leaving the jets is at least about Mach No. 2.

Claim 39

The process of claim 28, wherein the atomizing gas is argon.

Claim 40

The process of claim 28, wherein the teeming rate of the metal stream ranges from about 10 to 70 kg/min.

Claim 41

The process of claim 30, wherein the teeming rate of the metal stream ranges from about 25 to 50 kg/min.

Claim 42

The process of claim 37, wherein the nozzle through which the molten metal is teemed ranges in throat diameter from about 0.2 inch and up to about 0.375 inch.

Claim 43

The process of claim 30, wherein the gas is argon, the teeming rate of the molten metal through the nozzle ranges from about 10 to 70 kg/min., the throat diameter of the nozzle from about 0.2 inch to about 0.375 inch, and the kinetic energy generated at the exits of the jets is correlated with the argon driving pressure and jet throat diameter as set forth in FIG. 7.

Claim 44

A process for producing a spray cast metal ingot characterized by high density of substantially over 90% of the actual density of the metal which comprises: tapping a charge of molten metal into a tundish, teeming the metal from the tundish through a teeming nozzle to form a molten stream, allowing said molten metal stream to pass longitudinally and centrally through a hollow converging conical jet stream of super cooled non-oxidizing atomizing gas flowing at supersonic velocity produced by a plurality of jets substantially equally spaced in a circle with a first set of alternate jets projecting downwardly to define an included conical angle of impingement with said molten metal stream of less than about 30° and a second set of alternate jets projecting downwardly to define an included conical angle of at last 2° less than the angle formed by said first set, thereby providing a double impact mode system on said teeming molten metal stream in which the impingement produced by said second set of alternate jets is below the impingement produced by said first set of jets, such that, by virtue of said double mode impact, a relatively tight cone of atomized metal is produced having an included angle substantially less than 25°, directing said conically configurated atomized stream of metal into the interior of an ingot mold supported transverse to the path of said energetic metal stream with the longitudinal axis of said metal stream disposed at an acute angle of about 5° to 45° to the interior wall of said mold, causing said atomized stream of metal to scan the interior of said mold and strike the wall thereof at said acute angle while rotating said mold about its axis and oscillating said mold across the path of said stream to promote substantially uniform filling of said mold, and continuing the filling of said mold, thereby obtaining a compact high density spray cast ingot having an average density of substantially over 90% of the actual density of said metal.

Claim 45

A process for producing a spray cast metal ingot characterized by high density of substantially over 90% of the actual density of the metal which comprises: tapping a charge of molten metal into a tundish, teeming the metal from the tundish through a teeming nozzle to form a molten stream, allowing said molten metal stream to pass longitudinally and centrally through a hollow converging conical jet stream of super cooled non-oxidizing atomizing gas flowing at supersonic velocity produced by a plurality of jets substantially equally spaced in a circle with a first set of alternate jets projecting downwardly to define an included conical angle of impingement with said molten metal stream of less than about 30° and a second set of alternate jets projecting downwardly to define an included conical angle of at last 2° less than the angle formed by said first set, thereby providing a double impact mode system on said teeming molten metal stream in which the impingement produced by said second set of alternate jets is below the impingement produced by said first set of jets, such that, by virtue of said double mode impact, a relatively tight cone of atomized metal is produced having an included angle substantially less than 25°, directing said conically configurated atomized stream of metal into the interior of an ingot mold supported transverse to the path of said energetic metal stream with the longitudinal axis of said metal stream disposed at an acute angle of about 5° to 45° to the interior wall of said mold, causing said atomized stream of metal to scan the interior of said mold and strike the wall thereof at said acute angle while rotating said mold about its axis and oscillating said mold across the path of said stream to promote substantially uniform filling of said mold, and continuing the filling of said mold, thereby obtaining a compact high density spray cast ingot having an average density of substantially over 90% of the actual density of said metal.

Claim 46

The process of claim 41, wherein the arrangement of said first and second jets is such as to produce a highly energetic tight cone of atomized metal having an included angle not exceeding 20° and wherein the acute angle of the axis of the atomized metal stream with the interior wall of the mold ranges from about 5° to 25°.

Claim 47

The process of claim 42, wherein the arrangement of said first and second jets is such as to provide a tight cone of highly energetic stream of atomized metal having an included angle of about 5° to 15°.

Claim 48

The process of claim 43, wherein said tight cone of atomized metal has an included angle of about 5° to 10°.

Claim 49

The process of claim 41, wherein the temperature of the atomized metal stream reaching the mold ranges from about 85% of the absolute melting point of the metal to its absolute melting point.

Claim 50

The process of claim 41, wherein the exit velocity of the atomizing gas leaving the jets is at least about Mach No. 1.5.

Claim 51

The process of claim 46, wherein the exit velocity of the atomizing gas leaving the jets is at least about Mach No. 2.

Claim 52

The process of claim 41, wherein the atomizing gas is argon.

Claim 53

The process of claim 41, wherein the teeming rate of the metal stream ranges from about 10 to 70 kg/min.

Claim 54

The process of claim 42, wherein the teeming rate of the metal stream ranges from about 25 to 50 kg/min.

Claim 55

The process of claim 49, wherein the nozzle through which the molten metal is teemed ranges in throat diameter from about 0.2 inch up to about 0.375 inch.

Claim 56

The process of claim 42, wherein the gas is argon, the teeming rate of the molten metal through the nozzle ranges from about 10 to 70 kg/min., the throat diameter of the nozzle from about 0.2 inch to about 0.375 inch, and the kinetic energy generated at the exits of the jets is correlated with the argon driving pressure and jet throat diameter as set forth in FIG. 7.