Method for making optical fibers with variations in core diameter
Assignee: AT&T Inc
•
Filing: 1976-06-21
•
Granted: 1977-09-20
•
Expires: 1996-06-21
Abstract
Abstract A method is disclosed for producing optical fibers which are drawn with diameter variations in the transmitting core but with uniform overall diameter. In this process the glass starting member used in fabricating the optical fiber preform is etched with appropriate grooves. Additional glass is subsequently deposited on the etched starting member, and a fiber is drawn from the preform so fabricated.
Inventors
- 👤 William George French
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 10:43
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/14; C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/01205; C03B37/01225; C03B37/01228; C03B37/014; C03B37/01486; C03B37/01493; C03B37/018; C03B37/01861; G02B6/02; G02B6/02057; G02B6/02066; G02B6/028; G02B6/0288; C03B2203/00; C03B2203/10; C03B2203/18; C03B2203/20; C03B2203/22; C03B2203/36; G02B6/02214; Y; Y10; Y10S; Y10S359/00; Y10S359/90
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
76 words
A method for producing clad optical fibers with diameter variations in the transmitting core, but with uniform overall diameter, comprising: etching grooves around a cylindrical glass starting member, which grooves are approximately perpendicular to the axis of the starting member and with a periodicity between 0.5/R mm and 50/R mm; depositing additional glass on the etched starting member to form a glass member of uniform overall diameter; and drawing the structure so formed into a fiber.
Claim 2
Independent Claim
76 words
A method for producing clad optical fibers with diameter variations in the transmitting core, but with uniform overall diameter, comprising: etching grooves around a cylindrical glass starting member, which grooves are approximately perpendicular to the axis of the starting member and with a periodicity between 0.5/R mm and 50/R mm; depositing additional glass on the etched starting member to form a glass member of uniform overall diameter; and drawing the structure so formed into a fiber.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein the starting member is a hollow glass cylinder and the grooves are etched on the interior of the said cylinder.
Claim 4
Dependent Claim
21 words
The method of claim 2 wherein material is deposited on the etched glass cylinder using a modified chemical vapor deposition technique.
Claim 5
Dependent Claim
26 words
The method of claim 1 in which the starting member is a solid glass cylinder and grooves are etched on the exterior of the said cylinder.
Claim 6
Dependent Claim
18 words
The method of claim 4 wherein glass is formed on the etched cylinder using the soot deposition technique.
Claim 7
Dependent Claim
38 words
The method of claim 1 in which the etching proceeds by: depositing a resist on the glass cylinder, exposing the resist appropriately, developing the resist, removing partially the resist, etching the underlying glass, and removing the remaining resist.
Claim 8
Dependent Claim
11 words
The method of claim 1 wherein the resist is a photoresist.
Claim 9
Dependent Claim
13 words
The method of claim 7 wherein the photoresist is exposed using a laser.
Claim 10
Dependent Claim
14 words
The method of claim 7 wherein the photoresist is exposed using an interference pattern.
Claim 11
Dependent Claim
21 words
The method of claim 1 wherein the resist is an electron beam resist which is exposed with an appropriate electron beam.
Claim 12
Dependent Claim
42 words
The method of claim 1 wherein the starting member includes a layer of glass suitable for use in the fiber core, which layer of glass is etched with grooves whose depth is less than the thickness of the said layer of glass.
Claim 13
Dependent Claim
27 words
The method of claim 1 wherein at least a portion of the core material has radial, azimuthal or longitudinal variations in index of refraction, or combinations thereof.
References Cited (Backward Citations)
US3922062A
Cited
US3666348A
Cited
US3687514A
Cited
US3782914A
Cited
US3891302A
Cited
US3912478A
Cited
US3932160A
Cited
US3909110A
Cited
US3981705A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |