Aqueous coating composition of an acrylic polymer having reactive sites and an epoxy resin

Claim 2

An aqueous coating composition consisting essentially of about 25-50% by weight of film-forming constituents dispersed in an aqueous medium; wherein the film-forming constituents are a compatible mixture consisting essentially of (a) 60-95% by weight of an acrylic polymer of hard and soft segments having a number average molecular weight above 10,000 determined according to gel permeation chromatography and a glass transition temperature of -20° C. to +60° C.; and wherein the acrylic polymer consists essentially of polymerized units of 10-50% by weight of styrene, methyl styrene, methyl methacrylate or acrylonitrile, 40-89.5% by weight of an alkyl acrylate having 1-18 carbon atoms in the alkyl group or an alkyl methacrylate having 2-18 carbon atoms in the alkyl group, 0.5-10% by weight of an unsaturated carboxylic acid; and (b) 5-40% by weight of an epoxy resin having at least one terminal vic epoxide group in combination with at least one hydroxyl group or epoxide group or mixture thereof per polymer chain and having a number average molecular weight of 300 to 20,000 determined as above; wherein the composition contains sufficient basic compound to have a pH of about 5-10 and wherein the film-forming constituents in the fully cured state have a brittle ductile transition temperature of -40° C. to +20° C. measured at an elongation rate of 10% per minute on an Instron testing machine using a free film about 2-4 mils of the fully cured coating composition.

Claim 3

The coating composition of claim 1 containing pigment.

Claim 4

The coating composition of claim 1 in which the acrylic polymer has a number average molecular weight of about 25,000 to 70,000.

Claim 5

The coating composition of claim 3 in which the acrylic polymer consists essentially of polymerized units of about 30-40% by weight of methyl methacrylate, 50-65% by weight of ethyl acrylate, 5-10% by weight of acrylic acid.

Claim 6

The coating composition of claim 3 in which the epoxy resin has the structure ##STR5## where R is an alkylene group having 1-4 carbon atoms, n is an integer sufficiently large to provide a polymer having a number average molecular weight of 300 to 20,000.

Claim 7

An aqueous coating composition consisting essentially of about 25-50% by weight of film-forming constituents dispersed in an aqueous medium; wherein the film-forming constituents are a compatible mixture consisting essentially of (a) 60-95% by weight of an acrylic polymer of hard and soft segments having a number average molecular weight above 10,000 determined according to gel permeation chromatography and a glass transition temperature of -20° C. to +60° C., and wherein the acrylic polymer consists essentially of polymerized units of 10-50% by weight of styrene, methyl styrene, methyl methacrylate or acrylonitrile, 30-88.5% by weight of an alkyl methacrylate having 2-18 carbon atoms in the alkyl group or an alkyl acrylate having 1-18 carbon atoms in the alkyl group, 1-10% by weight of alkoxymethyl acrylamide or alkoxymethyl methacrylamide, 0.5-10% by weight of an unsaturated carboxylic acid; and (b) 5-40% by weight of an epoxy resin having at least one terminal vic epoxide group in combination with at least one hydroxyl group or epoxide group or mixture thereof per polymer chain and having a number average molecular weight of 300 to 20,000 determined as above; wherein the composition contains sufficient basic compound to have a pH of about 5-10 and wherein the film-forming constituents in the fully cured state have a brittle ductile transition temperature of -40° C. to +20° C. measured at an elongation rate of 10% per minute on an Instron testing machine using a free film about 2-4 mils of the fully cured coating composition.

Claim 8

An aqueous coating composition consisting essentially of about 25-50% by weight of film-forming constituents dispersed in an aqueous medium; wherein the film-forming constituents are a compatible mixture consisting essentially of (a) 60-95% by weight of an acrylic polymer of hard and soft segments having a number average molecular weight above 10,000 determined according to gel permeation chromatography and a glass transition temperature of -20° C. to +60° C., and wherein the acrylic polymer consists essentially of polymerized units of 10-50% by weight of styrene, methyl styrene, methyl methacrylate or acrylonitrile, 30-88.5% by weight of an alkyl methacrylate having 2-18 carbon atoms in the alkyl group or an alkyl acrylate having 1-18 carbon atoms in the alkyl group, 1-10% by weight of alkoxymethyl acrylamide or alkoxymethyl methacrylamide, 0.5-10% by weight of an unsaturated carboxylic acid; and (b) 5-40% by weight of an epoxy resin having at least one terminal vic epoxide group in combination with at least one hydroxyl group or epoxide group or mixture thereof per polymer chain and having a number average molecular weight of 300 to 20,000 determined as above; wherein the composition contains sufficient basic compound to have a pH of about 5-10 and wherein the film-forming constituents in the fully cured state have a brittle ductile transition temperature of -40° C. to +20° C. measured at an elongation rate of 10% per minute on an Instron testing machine using a free film about 2-4 mils of the fully cured coating composition.

Claim 9

The coating composition of claim 6 in which the acrylic polymer consists essentially of polymerized units of 10-25% by weight of styrene, 65-87.5% by weight of an alkyl acrylate having 2-4 carbon atoms in the alkyl group; 2-7% by weight of butoxymethyl acrylamide, 0.5-3% by weight of acrylic acid of methacrylic acid.

Claim 10

The coating composition of claim 1 having a pH of about 6.5-8.5 in which the film-forming constituents consist essentially of (a) 70-80% by weight, based on the weight of the film-forming constituents of an acrylic polymer consisting essentially of polymerized units of about 30-40% by weight of methyl methacrylate, 50-65% by weight of ethyl acrylate, 5-10% by weight of acrylic acid; (b) 20-30% by weight, based on the weight of the film-forming constituents, of an epoxy resin of the formula ##STR6## where n is a positive integer sufficiently large to provide a number average molecular weight of 1 300 to 20,000 and having an epoxide equivalent of 875-2500 and wherein wherein the basic compound is diethyl aminoethanol.