Heart valve with a sintered porous surface
Assignee: Baxter International Inc
•
Filing: 1976-06-03
•
Granted: 1977-04-19
•
Expires: 1996-06-03
Abstract
Abstract A unique sintering method of developing a controlled porosity, controlled thickness, metal layer on a metal substrate is disclosed. The region to be coated is cleaned, a suitable adhesive applied and appropriate metal powder poured on. Additional layers of adhesive and powder can be applied to give desired thickness. Pore size is determined by the size and shape of the powder particles and by the degree of sintering selected. Controlled sintering of the particles is carried out at a temperature near the melting point of the metal in a hydrogen atmosphere to permanently attach the particles to the substrate. The sintering is only sufficient to bond the particles while avoiding over-sintering which would close the porosity.No foreign material is left, the adhesive being burned off during sintering. The porous surface thus produced provides secure anchorage for the ingrowth of body tissue in a prosthetic device such as a heart valve or bone implant.
Inventors
- 👤 Ralph R. Kafesjian
- 👤 Norman G. Masse
- 👤 David P. Keller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 01:31
CPC Classifications
A; A61; A61F; A61F2/00; A61F2/02; A61F2/24; A61F2/2421; A61F2/2424; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
190 words
A heart valve having a metal orifice ring and cage struts confining a movable valve member, said valve member in closed position seating on a contact area of said orifice ring and in moving between closed and open positions engaging contact areas on said cage struts, said orifice ring and cage struts having surfaces exposed to a blood stream flowing through the valve and subject to the growth of connective tissue on said surfaces and a porous metal coating of controlled porosity and thickness sintered on said exposed metal surfaces other than said valve member contact areas to promote the ingrowth of said tissue so as to anchor the tissue to the metal in selected areas and prevent said tissue from breaking off and entering the blood stream, said coating comprising substantially a monolayer of sinterable metal particles of substantially uniform size and shape adhered to said selected areas and sintered on said selected areas, said particles being bonded to said arifice ring and cage struts and to each other without gross deformation of the particles so as to leave intercommunicating openings around the particles for said ingrowth of tissue.
Claim 2
Dependent Claim
190 words
A heart valve having a metal orifice ring and cage struts confining a movable valve member, said valve member in closed position seating on a contact area of said orifice ring and in moving between closed and open positions engaging contact areas on said cage struts, said orifice ring and cage struts having surfaces exposed to a blood stream flowing through the valve and subject to the growth of connective tissue on said surfaces and a porous metal coating of controlled porosity and thickness sintered on said exposed metal surfaces other than said valve member contact areas to promote the ingrowth of said tissue so as to anchor the tissue to the metal in selected areas and prevent said tissue from breaking off and entering the blood stream, said coating comprising substantially a monolayer of sinterable metal particles of substantially uniform size and shape adhered to said selected areas and sintered on said selected areas, said particles being bonded to said arifice ring and cage struts and to each other without gross deformation of the particles so as to leave intercommunicating openings around the particles for said ingrowth of tissue.
Claim 3
Dependent Claim
49 words
A heart valve as defined in claim 1 including a second discrete monolayer of metal particles of substantially uniform size and shape sintered on said first monolayer without gross deformation of the particles so as to leave intercommunicating openings around the particles extending through the thickness of the coating.
Claim 4
Dependent Claim
30 words
A heart valve as defined in claim 2 wherein the particles in said second monolayer are of substantially the same size and shape as the particles in said first monolayer.
Claim 5
Dependent Claim
28 words
A heart valve as defined in claim 2 wherein the particles in said second monolayer have a different size or shape than the particles in said first monolayer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-18 | 1980-10-18 | 1981-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-18 | 1984-10-18 | 1985-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-18 | 1988-10-18 | 1989-04-19 | $7700.00 | Window Closed / Lapsed |