Low durometer siloxane elastomers containing polytetrafluoroethylene powder
Assignee: Dow Silicones Corp
•
Filing: 1975-06-30
•
Granted: 1977-03-01
•
Expires: 1995-06-30
Abstract
Abstract When a small amount of polytetrafluoroethylene powder is mixed with certain curable polydiorganosiloxane compositions containing a reinforcing silica and an organic peroxide curing agent and the resulting mixture is extruded and heat-cured, the resulting elastomeric article has a durometer of less than 30 and has a greatly reduced amount of porosity or bubbles.
Inventors
- 👤 John D. Blizzard
- 👤 Carl M. Monroe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:20
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08K; C08K3/00; C08K3/34; C08K3/36; C08K5/00; C08K5/04; C08K5/14; C08L27/00; C08L27/02; C08L27/12; C08L27/18; C08G; C08G77/00; C08G77/04; C08G77/14; C08G77/16; C08G77/20; C08G77/22; C08G77/24
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
186 words
A composition consisting essentially of, a. 100 parts by weight of polydiorganosiloxane gum having a Williams plasticity of from 0.040 to 0.100 inches and having an average of from 1.999 to 2.001 organic radicals per silicon atom, at least 95 percent of the organic radicals being methyl, any remaining organic radical being selected from the group consisting of 3,3,3-trifluoropropyl and monovalent hydrocarbon radicals having from 1 to 6 carbon atoms, no more than 0.1 percent of all organic radicals in (a) having aliphatic unsaturation, said gum being endblocked with radicals selected from the group consisting of silicon-bonded hydroxyl radicals and silicon-bonded vinyl radicals, b. from 15 to 25 parts by weight of a reinforcing silica filler having a surface area of at least 50 square meters per gram, c. from 0.3 to 1.0 parts by weight, for every 100 parts by weight of the total of (a) plus (b) of a polytetrafluoroethylene powder having an average particle diameter of less than 1,000 microns and, d. from 0 to 3.0 percent by weight, based on the total weight of said composition of a organic peroxide curing agent.
Claim 2
Dependent Claim
186 words
A composition consisting essentially of, a. 100 parts by weight of polydiorganosiloxane gum having a Williams plasticity of from 0.040 to 0.100 inches and having an average of from 1.999 to 2.001 organic radicals per silicon atom, at least 95 percent of the organic radicals being methyl, any remaining organic radical being selected from the group consisting of 3,3,3-trifluoropropyl and monovalent hydrocarbon radicals having from 1 to 6 carbon atoms, no more than 0.1 percent of all organic radicals in (a) having aliphatic unsaturation, said gum being endblocked with radicals selected from the group consisting of silicon-bonded hydroxyl radicals and silicon-bonded vinyl radicals, b. from 15 to 25 parts by weight of a reinforcing silica filler having a surface area of at least 50 square meters per gram, c. from 0.3 to 1.0 parts by weight, for every 100 parts by weight of the total of (a) plus (b) of a polytetrafluoroethylene powder having an average particle diameter of less than 1,000 microns and, d. from 0 to 3.0 percent by weight, based on the total weight of said composition of a organic peroxide curing agent.
Claim 3
Dependent Claim
21 words
The composition of claim 1 wherein the organic peroxide curing agent is present in from 0.3 to 2.0 percent by weight.
Claim 4
Dependent Claim
79 words
The composition of claim 1 wherein the polydiorganosiloxane gum is a polydimethylsiloxane having hydroxyl endblocks and vinyl endblocks and having a Williams plasticity of from approximately 0.055 to approximately 0.075 inches, and a copolymer fluid is present in approximately 3 parts by weight for every 100 parts by weight of gum, said copolymer fluid consisting essentially of dimethylsiloxane units and methylvinylsiloxane units and having vinyl endblocks and having a viscosity of from 5,000 to 50,000 centipoise at 25° C.
Claim 5
Dependent Claim
34 words
The composition of claim 3 wherein the silica has a surface area of from 200 to 400 square meters per gram, the surface of said silica bearing an anticrepe-hardening agent for silica surface treatment.
Claim 6
Dependent Claim
23 words
The composition of claim 4 wherein the organic peroxide curing agent is present in from approximately 0.3 to approximately 2.0 percent by weight.
Claim 7
Dependent Claim
33 words
The composition according to claim 1 wherein (a) has a Williams plasticity of from 0.055 to 0.075 inches and from 0.01 to 0.05 percent of all organic radicals in (a) are vinyl radicals.
Claim 8
Dependent Claim
53 words
The composition according to claim 6 wherein the silica has a surface area of from 200 to 400 square meters per gram, the surface of said silica bearing an anticrepe-hardening agent for silica surface treatment and the organic peroxide curing agent is present in from approximately 0.3 to approximately 2.0 percent by weight.
Claim 9
Dependent Claim
11 words
A cured elastomer obtained by heating the composition of claim 2.
Claim 10
Dependent Claim
11 words
A cured elastomer obtained by heating the composition of claim 5.
Claim 11
Dependent Claim
11 words
A cured elastomer obtained by heating the composition of claim 7.
Claim 12
Dependent Claim
15 words
The composition of claim 5 wherein the anticrepe-hardening agent for silica surface treatment is hexamethyldisilazane.
Claim 13
Dependent Claim
11 words
A cured elastomer obtained by heating the composition of claim 11.
Claim 14
Dependent Claim
36 words
The composition of claim 7 wherein the anticrepe-hardening agent for silica surface treatment consists essentially of a hydroxyl-endblocked polydiorganosiloxane of less than 10 polydiorganosiloxane units per molecule and having diphenylsiloxane units, dimethylsiloxane units and methylvinylsiloxane units.
Claim 15
Dependent Claim
11 words
A cured elastomer obtained by heating the composition of claim 13.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-29 | 1980-08-30 | 1981-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-29 | 1984-08-30 | 1985-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-29 | 1988-08-30 | 1989-03-01 | $7700.00 | Window Closed / Lapsed |