Thin-film field-emission electron source and a method for manufacturing the same
Assignee: Hitachi Ltd
•
Filing: 1975-08-18
•
Granted: 1977-02-15
•
Expires: 1995-08-18
Abstract
Abstract A thin-film field-emission electron source having an emitter within a minute cavity in a conductive substrate, an insulating layer covering the surface of the substrate except for the portion of the cavity, and a first anode layer on the insulating layer, wherein the substrate and the emitter are comprised as one body, and the insulating layer and the first anode layer overhang the cavity, except directly over the emitter. This electron source may be manufactured by the method comprising the steps of i) forming a sandwich structure of the substrate-insulating layer-first anode layer, ii) forming a closed loop opening at a predetermined position on the surface of the first anode layer, iii) etching the insulating layer with the use of the first anode layer as a mask and iv) forming an emitter and a cavity by etching the substrate with the use of the insulating layer as a mask. This thin-film field-emission electron source can be manufactured very readily and has good insulation between the emitter and the first anode layer.
Inventors
- 👤 Isamu Yuito
- 👤 Kikuji Sato
- 👤 Mikio Hirano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:35
CPC Classifications
H; H01; H01J; H01J1/00; H01J1/02; H01J1/30; H01J1/304; H01J1/3042; H01J9/00; H01J9/02; H01J9/022; H01J9/025
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
78 words
A thin-film field-emission electron source comprising a conductive substrate having a minute cavity, a needlelike emitter within said cavity, an insulating layer on the surface of said substrate except for the portion of said cavity, and a first anode layer on said insulating layer, wherein said emitter and said substrate are formed as a single body, and said insulating layer and said first anode layer overhang said cavity around the projection of said emitter except over said emitter.
Claim 2
Dependent Claim
78 words
A thin-film field-emission electron source comprising a conductive substrate having a minute cavity, a needlelike emitter within said cavity, an insulating layer on the surface of said substrate except for the portion of said cavity, and a first anode layer on said insulating layer, wherein said emitter and said substrate are formed as a single body, and said insulating layer and said first anode layer overhang said cavity around the projection of said emitter except over said emitter.
Claim 3
Dependent Claim
27 words
The thin-film field-emission electron source of claim 1, in which said substrate is composed of an insulating plate and a conductive layer formed on said insulating plate.
Claim 4
Dependent Claim
31 words
The thin-film field-emission electron source of claim 1, in which said substrate is made of a material selected from the group consisting of Si, W, W alloyed with Th, and Mo.
Claim 5
Dependent Claim
51 words
The thin-film field-emission electron source of claim 1, in which said insulating layer is made of a material selected from the group consisting of SiO 2 , TiO 2 , Ta 2 O 5 , Y 2 O 3 , Si 3 N 4 , AlN, alumina and heat resisting glass.
Claim 6
Dependent Claim
85 words
The thin-film field-emission electron source of claim 1, in which the surface of said emitter is coated with a material selected from the group consisting of (Ba,Sr)O, (BaO--SrO--CaO), (Ca,Sr)O, LaB 6 , CaB 6 , SrB 6 , BaB 6 , CeB 6 , (La,Sr)B 6 , (La,Ba)B 6 , (La,Eu)B 6 , (Ce,Sr)B 6 , (Ce,Ba)B 6 , (Ce,Eu)B 6 , (Pr,Sr)B 6 , (Pr,Ba)B 6 , (Pr,Eu)B 6 , (Nd,Sr)B 6 , (Nd,Ba)B 6 , (Nd,Eu)B 6 , (Eu,Sr)B 6 and (Eu,Ba)B.sub. 6.
Claim 7
Dependent Claim
31 words
The thin-film field-emission electron source of claim 1, in which said first anode layer is made of a material selected from the group consisting of Cr, Au, Ni and their alloys.
Claim 8
Dependent Claim
27 words
The thin-film field-emission electron source of claim 5, in which the first anode layer is made of the same material as said surface of said coated emitter.
Claim 9
Dependent Claim
112 words
The method for manufacturing the thin-film field-emission electron source according to claim 1, comprising the steps: i) forming an insulating layer on a conductive substrate, ii) forming a first anode layer made of a conductive material on said insulating layer, iii) forming an annular opening at a predetermined position on said first anode layer by etching, iv) forming an annular opening on the face of said insulating layer under the opening provided in step iii) by etching said insulating layer employing said first anode layer as a mask, and v) forming a minute cavity and a needlelike emitter on said substrate by etching said substrate employing said insulating layer as a mask.
Claim 10
Dependent Claim
18 words
The method of claim 8, in which said insulating layer is formed by a chemical vapor deposition method.
Claim 11
Dependent Claim
17 words
The method of claim 8, in which said insulating layer is formed by a thermal oxydization method.
Claim 12
Dependent Claim
16 words
The method of claim 8, in which said insulating layer is formed by a sputtering method.
Claim 13
Dependent Claim
17 words
The method of claim 8, in which said first anode layer is formed by an evaporation method.
Claim 14
Dependent Claim
21 words
The method of claim 8, in which said etchings of steps iii), iv) and/or v) are carried out by chemical etching.
Claim 15
Dependent Claim
21 words
The method of claim 8, in which said etchings of steps iii), iv) and/or v) are carried out by physical etching.
Claim 16
Dependent Claim
23 words
The method of claim 8, further comprising a step of depositing an electron emissive material layer on said emitter after said step v).
Claim 17
Dependent Claim
78 words
A method for manufacturing the thin-film field-emission electron source according to claim 1, comprising the steps: i) forming an insulating layer on a conductive substrate, ii) forming an annular opening at a predetermined position on said insulating layer by etching, iii) forming a minute cavity and a needlelike emitter on said substrate by etching said substrate employing said insulating layer as a mask, and iv) depositing an electron emissive material layer on said insulating layer and said emitter.
Claim 18
Dependent Claim
24 words
The thin-film field-emission electron source of claim 1, in which the numbers of said cavities, said emitters and said first anode layers are plural.
Claim 19
Dependent Claim
24 words
The thin-film field-emission electron source of claim 1, in which the overhang of said insulating layer over said cavity is greater than 0.5 μm.
Claim 20
Dependent Claim
17 words
The thin-film field-emission electron source of claim 18, in which said overhang is greater than 1 μm.
References Cited (Backward Citations)
US3453478A
Cited
US3500102A
Cited
US3755704A
Cited
US3665241A
Cited
US3671798A
Cited
US3814968A
Cited
US3855499A
Cited
US3970887A
Cited
US3921022A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-15 | 1980-08-16 | 1981-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-15 | 1984-08-16 | 1985-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-15 | 1988-08-16 | 1989-02-15 | $7700.00 | Window Closed / Lapsed |