Method of making glass ampul for jet injector
Assignee: GlaxoSmithKline LLC
•
Filing: 1975-06-19
•
Granted: 1976-10-12
•
Expires: 1995-06-19
Abstract
Abstract A method of forming an ampul comprises drawing an aluminosilicate glass tube containing alkali metal ions and having the inner and outer diameter desired for the body of the ampul to reduce the diameter and provide a portion having an inner diameter in the range of from about 0.007 to about 0.03 cm. Advantageously the transition shoulder portion extending from the full diameter to the reduced diameter is heated while rotating and then subjected to axial compression to partially collapse it. The reduced diameter portion of the tube is then severed to form an ampul with a body having the inner and outer diameters of the original tube and a discharge passage which has a discharge opening with a diameter in the range of from about 0.007 to about 0.03 cm. and which has a length at least ten times the diameter of the discharge opening. The drawing provides for a small taper in the discharge passage which preferably will have a diameter equal to from about 2 to about 1 times the diameter of the discharge opening. Alternatively, the drawing operation additionally provides a portion tapering gradually to an inner diameter smaller than the desired diameter of the discharge opening and, after the severing operation, the last-mentioned portion is removed by grinding to provide a discharge opening of the desired size.
Inventors
- 👤 Russell B. Bennett
- 👤 Clair E. Campbell
- 👤 Howard B. Pritz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:54
CPC Classifications
C; C03; C03C; C03C21/00; C03C21/001; C03B; C03B23/00; C03B23/04; C03B23/11; C03C21/007; C03C21/008; Y; Y10; Y10T; Y10T428/00; Y10T428/31; Y10T428/315
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
176 words
The method of forming a glass jet injector ampul having a body open at one end and having a restricted discharge passage at the other end with a discharge opening of a diameter of from about 0.007 to about 0.03 cm. comprising: drawing an aluminosilicate glass tube containing alkali metal ions and having the inner and outer diameter desired for the body of the ampul to provide a major reduction in the diameter of a portion of the tube to provide a portion having an inner diameter in the range of from about 0.007 to about 0.03 cm., heating the transition portions extending between the full diameter of the tube and the reduced diameter portion while rotating the tube and compressing the tube axially to partially collapse said portions, severing the reduced diameter portion of the tube to form an ampul with a body having the inner and outer diameters of the original tube and a discharge passage having a discharge opening having a diameter in the range of from about 0.007 to about 0.03 cm.
Claim 2
Independent Claim
176 words
The method of forming a glass jet injector ampul having a body open at one end and having a restricted discharge passage at the other end with a discharge opening of a diameter of from about 0.007 to about 0.03 cm. comprising: drawing an aluminosilicate glass tube containing alkali metal ions and having the inner and outer diameter desired for the body of the ampul to provide a major reduction in the diameter of a portion of the tube to provide a portion having an inner diameter in the range of from about 0.007 to about 0.03 cm., heating the transition portions extending between the full diameter of the tube and the reduced diameter portion while rotating the tube and compressing the tube axially to partially collapse said portions, severing the reduced diameter portion of the tube to form an ampul with a body having the inner and outer diameters of the original tube and a discharge passage having a discharge opening having a diameter in the range of from about 0.007 to about 0.03 cm.
Claim 3
Dependent Claim
31 words
The method of claim 1 in which after the drawing the reduced diameter portion has an outer diameter reduced by from about 45 to about 70% of its original outer diameter.
Claim 4
Dependent Claim
14 words
The method of claim 1 in which the aluminosilicate glass is an aluminoborosilicate glass.
Claim 5
Independent Claim
148 words
The method of forming a glass jet injector ampul having a body open at one end and having a restricted discharge passage at the other end with a discharge opening of a diameter of from about 0.007 to about 0.03 cm comprising: drawing an aluminisilicate glass tube containing alkali metal ions and having the inner and outer diameter desired for the body of the ampul to provide a major reduction in the diameter of a portion of the tube to provide a portion having an inner diameter smaller then a predetermined inner diameter in the range of from about 0.007 to about 0.03 cm., severing the reduced diameter portion of the tube to form an ampul with a body having the inner and outer diameters of the original tube, grinding back the severed end of the tube until the predetermined inner diameter of the discharge opening is provided.
Claim 6
Independent Claim
148 words
The method of forming a glass jet injector ampul having a body open at one end and having a restricted discharge passage at the other end with a discharge opening of a diameter of from about 0.007 to about 0.03 cm comprising: drawing an aluminisilicate glass tube containing alkali metal ions and having the inner and outer diameter desired for the body of the ampul to provide a major reduction in the diameter of a portion of the tube to provide a portion having an inner diameter smaller then a predetermined inner diameter in the range of from about 0.007 to about 0.03 cm., severing the reduced diameter portion of the tube to form an ampul with a body having the inner and outer diameters of the original tube, grinding back the severed end of the tube until the predetermined inner diameter of the discharge opening is provided.
Claim 7
Dependent Claim
41 words
The method of claim 4 in which before severing the transition portions extending between the full diameter of the tube and the reduced diameter portion are heated while being rotated and the tube is compressed axially to partially collapse said portions.
Claim 8
Dependent Claim
14 words
The method of claim 5 in which the aluminosilicate glass is an aluminoborosilicate glass.
References Cited (Backward Citations)
US1888635A
Cited
US2151840A
Cited
US2090861A
Cited
US2392104A
Cited
US3091104A
Cited
US3790430A
Cited
US3445316A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-12 | 1980-04-12 | 1980-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-12 | 1984-04-12 | 1984-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-12 | 1988-04-12 | 1988-10-12 | $7700.00 | Window Closed / Lapsed |