US3975478A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing highly permeable acrylic hollow fibers
Assignee: Permea Inc
•
Filing: 1974-08-14
•
Granted: 1976-08-17
•
Expires: 1994-08-14
Abstract
Abstract A method is provided for fabricating asymmetric acrylic hollow fibers for use in separatory processes as a selective membrane. The fibers are highly permeable and exhibit a high degree of selectivity in discriminating mixtures into their various components. The fibers are formed by extruding an acrylic polymer solution through an annular orifice while simultaneously injecting a coagulating fluid into the bore of the fiber extrudate as it is formed. The extrusion may be directly into a coagulating bath maintained at a temperature of from 60 DEG to 80 DEG C. or alternatively the freshly extruded fiber may be first passed through an air space (evaporation zone) and thence into the coagulating bath. Following coagulation, the fibers are water washed to remove residual solvent.
Inventors
- 👤 Richard L. Leonard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 03:22
CPC Classifications
B; B01; B01D; B01D61/00; B01D61/36; B01D61/362; B01D69/00; B01D69/08; B01D71/00; B01D71/06; B01D71/40; B01D71/42; D; D01; D01D; D01D5/00; D01D5/24; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2973; Y10T428/2975; Y10T428/2978
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
115 words
A method for forming an asymmetric hollow acrylic fiber having an axially disposed cylindrical bore extending throughout the fiber length and characterized by a high permeability and selectivity when used as a separatory membrane, the method which comprises: extruding a solution of fiber-forming acrylic polymer which contains at least 70 percent by weight acrylonitrile through a shaping orifice to form a hollow fiber while simultaneously injecting a coagulating fluid into the fiber bore as it is formed, causing the extruded fiber to contact a coagulation bath maintained at a temperature of from about 60° to 80°C. immediately upon exiting from said shaping orifice and thereafter washing said hollow fiber with water to remove residual solvent.
Claim 2
Independent Claim
115 words
A method for forming an asymmetric hollow acrylic fiber having an axially disposed cylindrical bore extending throughout the fiber length and characterized by a high permeability and selectivity when used as a separatory membrane, the method which comprises: extruding a solution of fiber-forming acrylic polymer which contains at least 70 percent by weight acrylonitrile through a shaping orifice to form a hollow fiber while simultaneously injecting a coagulating fluid into the fiber bore as it is formed, causing the extruded fiber to contact a coagulation bath maintained at a temperature of from about 60° to 80°C. immediately upon exiting from said shaping orifice and thereafter washing said hollow fiber with water to remove residual solvent.
Claim 3
Dependent Claim
19 words
The method in accordance with claim 1, wherein said fiber-forming polymer is a copolymer of acrylonitrile and vinyl acetate.
Claim 4
Dependent Claim
32 words
The method in accordance with claim 1, wherein said injected coagulating fluid is selected from the group consisting of water, an aqueous solution of ethanol and an aqueous solution of ethylene glycol.
Claim 5
Dependent Claim
18 words
The method in accordance with claim 1, wherein said coagulation bath consists of an aqueous solution of dimethylacetamide.
Claim 6
Independent Claim
132 words
A method for forming an asymmetric hollow acrylic fiber having an axially disposed cylindrical bore extending throughout the fiber length and characterized by a high permeability and selectivity when used as a separatory membrane, the method which comprises: extruding a solution of fiber-forming acrylic polymer which contains at least 70 percent by weight acrylonitrile through a shaping orifice to form a hollow fiber while simultaneously injecting a coagulating fluid into the fiber bore as it is formed, causing the extruded fiber to pass through a zone of air for a period of from about 0.01 to 1.0 second upon emerging from said shaping orifice followed by passage through a coagulation bath maintained at a temperature of from 60° to 80°C., and thereafter washing said hollow fiber with water to remove residual solvent.
Claim 7
Independent Claim
132 words
A method for forming an asymmetric hollow acrylic fiber having an axially disposed cylindrical bore extending throughout the fiber length and characterized by a high permeability and selectivity when used as a separatory membrane, the method which comprises: extruding a solution of fiber-forming acrylic polymer which contains at least 70 percent by weight acrylonitrile through a shaping orifice to form a hollow fiber while simultaneously injecting a coagulating fluid into the fiber bore as it is formed, causing the extruded fiber to pass through a zone of air for a period of from about 0.01 to 1.0 second upon emerging from said shaping orifice followed by passage through a coagulation bath maintained at a temperature of from 60° to 80°C., and thereafter washing said hollow fiber with water to remove residual solvent.
Claim 8
Dependent Claim
19 words
The method in accordance with claim 5, wherein said fiber-forming polymer is a copolymer of acrylonitrile and vinyl acetate.
Claim 9
Dependent Claim
32 words
The method in accordance with claim 5, wherein said injected coagulating fluid is selected from the group consisting of water, an aqueous solution of ethanol and an aqueous solution of ethylene glycol.
Claim 10
Dependent Claim
18 words
The method in accordance with claim 5, wherein said coagulation bath consists of an aqueous solution of dimethylacetamide.
Claim 11
Dependent Claim
14 words
The method in accordance with claim 5, wherein said coagulation bath consists of water.
References Cited (Backward Citations)
US3674628A
Cited
US3799356A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |