Altering gas permeabilities of polymeric material
Assignee: Dow Silicones Corp
•
Filing: 1973-08-03
•
Granted: 1976-08-17
•
Expires: 1993-08-03
Abstract
Abstract The gas permeability of a polymeric material is altered by irreversibly mechanically stressing in at least one direction a polymeric material which is a mixture of two phases where one phase is evenly distributed throughout a second phase and one phase is present in an amount of at least 10 weight percent. The phases are polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature, are chemically dissimilar materials and have oxygen gas permeabilities which differ by a factor of at least 10. At least one phase is a thermoplastic which is solid at ambient temperature and the mixture retains its physical state on standing at ambient temperature over extended periods of time. An example would be cold rolling a sheet of a polyblend of polyethylene and polydimethylsiloxane. Mechanically stressing film in at least one direction by cold rolling, drawing or blowing polymeric materials as defined above alters the gas permeability from unstressed film. An extruded tube of polymeric material mechanically stressed in at least one direction has altered gas permeability compared to an unstressed tube.
Inventors
- 👤 James R. Falender
- 👤 Sarah E. Lindsey
- 👤 Andrew H. Ward
- 👤 Thomas C. Kendrick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:02
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0002; B01D67/0023; B01D67/0025; B01D67/0027; B01D71/00; B01D71/06; B01D71/70; B01D71/701; C; C08; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/20; C08G77/22; C08G77/24; C08G77/42; C08G77/44; C08G77/70; Y; Y10; Y10S; Y10S260/00; Y10S260/32; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1397
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
276 words
A method for altering the gas permeability of a polymeric material comprising irreversibly mechanically stressing said polymeric material in at least one direction at a suitable processing temperature and thereafter reducing the temperature within a suitable time period to retain molecular orientation within said polymeric material which had been oriented by said stressing and where oxygen gas permeability is increased, said polymeric material consisting essentially of a mixture of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 2
Independent Claim
276 words
A method for altering the gas permeability of a polymeric material comprising irreversibly mechanically stressing said polymeric material in at least one direction at a suitable processing temperature and thereafter reducing the temperature within a suitable time period to retain molecular orientation within said polymeric material which had been oriented by said stressing and where oxygen gas permeability is increased, said polymeric material consisting essentially of a mixture of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 3
Dependent Claim
27 words
The method in accordance with claim 1 in which the second phase is selected from the group consisting of a hydrocarbon polymer, hydrocarbon copolymers and mixtures thereof.
Claim 4
Dependent Claim
27 words
The method in accordance with claim 2 in which the polydiorganosiloxane is a copolymer of dimethylsiloxane units and methylvinyl siloxane units and the second phase is polyethylene.
Claim 5
Dependent Claim
30 words
The method in accordance with claim 2 in which the polydiorganosiloxane is a polydimethylsiloxane and the second phase is a hydrocarbon copolymer derived from monomeric units of styrene and alphamethylstyrene.
Claim 6
Dependent Claim
23 words
The method in accordance with claim 1 in which two perceptibly distinct phases are chemically bonded in the form of a block copolymer.
Claim 7
Dependent Claim
28 words
The method in accordance with claim 5 in which the block copolymer consists essentially of thermoplastic blocks of polyalphamethylstyrene capped with short chain polystyrene blocks and polydimethylsiloxane blocks.
Claim 8
Dependent Claim
240 words
A film comprising two polymeric materials having mechanically stressed molecular orientation in at least one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil) (24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 9
Dependent Claim
240 words
A film comprising two polymeric materials having mechanically stressed molecular orientation in at least one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil) (24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 10
Dependent Claim
24 words
The film in accordance with claim 7 which is a cold rolld film having increased oxygen gas permeability over a compositionally equivalent unstressed film.
Claim 11
Dependent Claim
240 words
An extruded tube comprising two polymeric materials having mechanically stressed molecular orientation in at least one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 12
Dependent Claim
240 words
An extruded tube comprising two polymeric materials having mechanically stressed molecular orientation in at least one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 13
Dependent Claim
240 words
A drawn film comprising two polymeric materials having mechanically stressed molecular orientation in at least one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 14
Dependent Claim
240 words
A drawn film comprising two polymeric materials having mechanically stressed molecular orientation in at least one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, said polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 15
Dependent Claim
240 words
A blown film comprising two polymeric materials having mechanically stressed molecular orientation in more than one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, and polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 16
Dependent Claim
240 words
A blown film comprising two polymeric materials having mechanically stressed molecular orientation in more than one direction and having an oxygen gas permeability increased from a compositionally equivalent unstressed mixture consisting essentially of two perceptibly distinct phases wherein one phase is evenly distributed throughout a second phase in which said distributed phase is a polydiorganosiloxane wherein the organic groups are selected from the group consisting essentially of methyl, ethyl, vinyl, phenyl and 3,3,3-trifluoropropyl radicals where at least 50 percent of the organic groups are methyl or ethyl radicals and in which said distributed phase particles have diameters perpendicular to the longitudinal axis of less than 100 microns and in which one phase is present in an amount of at least 10 weight percent where the total weight of all the phases is 100 weight percent, said phases being polymeric materials which each have an elastic shear modulus of less than 10 9 dynes per square centimeter at processing temperature and which are flowable at processing temperatures, and polymeric materials of the phases being chemically dissimilar materials having oxygen gas permeabilities which differ by a factor of at least 10 wherein said gas permeabilities are in units of cm 3 (mil)/(24 hr) (100 in 2 ) (atm), one phase being a thermoplastic polymeric material which is a solid at ambient temperature, and said mixture retaining the above stated physical state on standing at ambient temperature over an extended period of time.
Claim 17
Dependent Claim
41 words
The blown film in accordance with claim 11 in which two perceptibly distinct phases are chemically bonded in the form of a block copolymer which consists essentially of thermoplastic blocks of polyalphamethylstyrene capped with short chain polystyrene blocks and polydimethylsiloxane blocks.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |