Method of producing polymer compositions based on chlorinated polyethylene
Assignee: Resonac Holdings Corp
•
Filing: 1975-01-28
•
Granted: 1976-07-20
•
Expires: 1995-01-28
Abstract
Abstract In a method for producing a polymer composition by contacting A. a polymer component selected from the group consisting of chlorinated polyethylene and a mixture consisting of a major amount of chlorinated polyethylene and a minor amount of copolymer selected from an ethylene-propylene copolymer rubber an, ethylene-propylene-nonconjugated diene terpolymer rubber and an ethylene-vinyl acetate copolymer rubber, with B. a monomer mixture comprising B1. AT LEAST ONE OF STYRENE, ALPHA-METHYL STYRENE, TERTIARY BUTYL STYRENE AND CHLOROSTYRENE, AND B2. AT LEAST ONE OF ACRYLONITRILE AND METHACRYLONITRILE UNDER POLYMERIZATION CONDITIONS TO FORM AN INTERPOLYMER OF THE COMPONENTS (A) and (B), the improvement which comprises suspending polymer component (A) and monomer component (B) in the form of fine particles in an aqueous medium.
Inventors
- 👤 Akira Takahashi
- 👤 Hiroo Kojima
- 👤 Masao Ogawa
- 👤 Hiroshi Osuka
- 👤 Shoichi Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:48
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08F; C08F255/00; C08F255/02; C08F255/023; C08L51/00; C08L51/06; Y; Y10; Y10S; Y10S260/00; Y10S260/14; Y10S525/00; Y10S525/903
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
213 words
A method for producing a blended polymer composition comprising blending I. an interpolymer prepared by contacting A. a polymer component selected from the group consisting of chlorinated polyethylene of a degree of chlorination of 10-50 percent and a mixture consisting of 50-90 percent by weight of said chlorinated polyethylene and 10-50% by weight of a copolymer selected from an ethylene-propylene copolymer rubber, an ethylene-propylene-nonconjugated diene terpolymer rubber and an ethylene-vinyl acetate copolymer rubber, with B. a monomer mixture comprising b 1 . at least one monomer selected from styrene, alpha-methyl styrene, t-butyl styrene and chloro-styrene and b 2 . at least one monomer selected from acrylonitrile and methacrylonitrile under polymerization conditions in the presence of a polymerization initiator to form an interpolymer of components (A) and (B) wherein the polymer component (A) and monomer component (B) are suspended in the form of fine particles in a state of separation from each other in an aqueous medium, said component (A) having a particle size of 5-150 Tyler mesh, the weight ratio of said component (A) to component (B) ranging from about 10:90 to about 90:10 with Ii. a polymer separately prepared from said component (B), the overall weight ratio of component (A) to component (B) in said blended copolymer being from 5:95 to 50:50.
Claim 2
Independent Claim
213 words
A method for producing a blended polymer composition comprising blending I. an interpolymer prepared by contacting A. a polymer component selected from the group consisting of chlorinated polyethylene of a degree of chlorination of 10-50 percent and a mixture consisting of 50-90 percent by weight of said chlorinated polyethylene and 10-50% by weight of a copolymer selected from an ethylene-propylene copolymer rubber, an ethylene-propylene-nonconjugated diene terpolymer rubber and an ethylene-vinyl acetate copolymer rubber, with B. a monomer mixture comprising b 1 . at least one monomer selected from styrene, alpha-methyl styrene, t-butyl styrene and chloro-styrene and b 2 . at least one monomer selected from acrylonitrile and methacrylonitrile under polymerization conditions in the presence of a polymerization initiator to form an interpolymer of components (A) and (B) wherein the polymer component (A) and monomer component (B) are suspended in the form of fine particles in a state of separation from each other in an aqueous medium, said component (A) having a particle size of 5-150 Tyler mesh, the weight ratio of said component (A) to component (B) ranging from about 10:90 to about 90:10 with Ii. a polymer separately prepared from said component (B), the overall weight ratio of component (A) to component (B) in said blended copolymer being from 5:95 to 50:50.
Claim 3
Dependent Claim
149 words
The method of claim 1 which further comprises blending said composition with (III) an interpolymer prepared by contacting A'. a copolymer selected from the group consisting of ethylene-propylene copolymer rubber, ethylene-propylene-nonconjugated diene terpolymer rubber and ethylene-vinyl acetate copolymer rubber, with B'. a monomer mixture comprising b 1 '. at least one monomer selected from styrene, alpha-methylstyrene, t-butyl styrene and chlorostyrene, and b 2 '. at least one monomer selected from acrylonitrile and methacrylonitrile under polymerization conditions in the presence of a polymerization initiator to form an interpolymer of components (A') and (B'), wherein said copolymer component (A') and monomer component (B') are suspended in the form of fine particles in a state of separation from each other in an aqueous medium, said component (A') having a particle size of 5-150 Tyler mesh, the weight ratio of said component (A') to component (B') ranging from about 10:90 to about 90:10.
Claim 4
Independent Claim
202 words
A method of preparing a polymer composition which comprises blending (I) an interpolymer prepared by contacting A. a polymer component selected from the group consisting of chlorinated polyethylene of a degree of chlorination of 10-50 percent and a mixture consisting of 50-90 percent by weight of said chlorinated polyethylene and 10-50 percent by weight of copolymer selected from an ethylene-propylene copolymer rubber, an ethylene-propylene-conconjugated diene terpolymer rubber and an ethylene-vinyl acetate copolymer rubber with B. a monomer mixture comprising b 1 . at least one monomer selected from styrene, alpha-methyl styrene, t-butyl styrene and chlorostyrene and b 2 . at least one monomer selected from acrylonitrile and methacrylonitrile under polymerization conditions in the presence of a polymerization initiator to form an interpolymer of components (A) and (B) wherein the polymer component (A) and monomer component (B) are suspended in the form of fine particles in a state of separation from each other in an aqueous medium, said component (A) having a particle size of 5-150 Tyler mesh, the weight ratio of said component (A) to component (B) ranging from about 10:90 to about 65:35 with (II) from about 10-70 percent by weight based on the total composition of a polyvinyl chloride resin.
Claim 5
Independent Claim
202 words
A method of preparing a polymer composition which comprises blending (I) an interpolymer prepared by contacting A. a polymer component selected from the group consisting of chlorinated polyethylene of a degree of chlorination of 10-50 percent and a mixture consisting of 50-90 percent by weight of said chlorinated polyethylene and 10-50 percent by weight of copolymer selected from an ethylene-propylene copolymer rubber, an ethylene-propylene-conconjugated diene terpolymer rubber and an ethylene-vinyl acetate copolymer rubber with B. a monomer mixture comprising b 1 . at least one monomer selected from styrene, alpha-methyl styrene, t-butyl styrene and chlorostyrene and b 2 . at least one monomer selected from acrylonitrile and methacrylonitrile under polymerization conditions in the presence of a polymerization initiator to form an interpolymer of components (A) and (B) wherein the polymer component (A) and monomer component (B) are suspended in the form of fine particles in a state of separation from each other in an aqueous medium, said component (A) having a particle size of 5-150 Tyler mesh, the weight ratio of said component (A) to component (B) ranging from about 10:90 to about 65:35 with (II) from about 10-70 percent by weight based on the total composition of a polyvinyl chloride resin.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein the weight ratio of component (A) to component (B) in the interpolymer (I) ranges from 10:90 to 65:35.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said polymerization initiator is mixed in said component (B) prior to its suspension in the aqueous medium.
Claim 8
Dependent Claim
14 words
The method of claim 1 wherein the polymerization temperature ranges from 50°C to 150°C.
Claim 9
Dependent Claim
35 words
The method of claim 1 wherein said chlorinated polyethylene of component (A) is a polyethylene of a weight average molecular weight exceeding 100,000, which has been chlorinated to a degree of chlorination of 10-50 percent.
Claim 10
Dependent Claim
27 words
The method of claim 1 wherein said aqueous medium is used in an amount of 0.8 to 10-fold the total weight of said components (A) and (B).
Claim 11
Dependent Claim
24 words
The method of claim 1 wherein the weight ratio of component (A) to component (B) in the interpolymer (I) ranges from 10:90 to 50:50.
Claim 12
Dependent Claim
24 words
The method of claim 1 wherein the weight ratio of component (b 1 ) to component (b 2 ) ranges from 10:90 to 90:10.
Claim 13
Dependent Claim
33 words
The method of claim 1 wherein (b 1 ) is styrene and (b 2 ) is acrylonitrile and the ratio of (b 1 ) to (b 2 ) ranges from 10:90 to 35:65.
Claim 14
Dependent Claim
45 words
The method of claim 1 wherein component (A) is a mixture consisting of 50-90 percent by weight of said chlorinated polyethylene and 10-50 percent by weight of a copolymer selected from an ethylene-propylene copolymer rubber, an ethylene-propylene-nonconjugated diene terpolymer rubber and an ethylene-vinylacetate copolymer rubber.
Claim 15
Dependent Claim
17 words
The method of claim 1 wherein said component (A) has a particle size of 10-48 Tyler Mesh.
Claim 16
Dependent Claim
22 words
The method of claim 3 which contains about 15-30 percent by weight based on the total composition of said polyvinyl chloride resin.
Claim 17
Dependent Claim
23 words
The method of claim 3 wherein said polymerization initiator is mixed in said component (B) prior to its suspension in the aqueous medium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-20 | 1980-01-19 | 1980-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-20 | 1984-01-19 | 1984-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-20 | 1988-01-19 | 1988-07-20 | $7700.00 | Window Closed / Lapsed |