Light guide fabrication
Assignee: AT&T Inc
•
Filing: 1974-02-15
•
Granted: 1976-06-15
•
Expires: 1994-02-15
Abstract
Abstract A light guide is produced by the out-diffusion of boron oxide through a free surface of a uniform borosilicate mass. The resulting structure consists of increased index silica rich regions near the surface in contact with lower index regions of a composition approaching that of the unmodified borosilicate. The out-diffusion process, generally carried out at a temperature approaching the softening point of the glass, may be applied to a borosilicate tube to result in a fiber preform. Fibers drawn from such a preform may be characterized by a silica core region, a borosilicate clad region, and a silica outer shell. Use of the procedure results in a graded index structure.
Inventors
- 👤 Raymond Edward Jaeger
- 👤 John Burnette MacChesney
- 👤 Douglas Arthur Pinnow
- 👤 LeGrand Gerard Van Uitert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 09:44
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/01205; C03B37/014; C03B37/018; C03B37/01807; C03B37/01853; C03C; C03C13/00; C03C13/04; C03C13/045; C03C13/046; C03C21/00; C03C3/00; C03C3/04; C03C3/06; C03C3/076; C03C3/089; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2201/20; C03B2201/22; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/26; C03C2201/00; C03C2201/06; C03C2201/08; C03C2201/10; C03C2203/00; C03C2203/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
223 words
Process for fabricating a light guide which as fabricated comprises a body including a core region and a clad region, the refractive index being graded from a first value within the core region to a lesser value within the clad region in which the variation in refractive index is due to an increasing content of boron oxide, said increasing content corresponding in direction with decreasing refractive index, in which both core region and clad region are constituted of glass comprising heat treating a body consisting essentially of a borosilicate glass composition, said composition having a ratio of SiO 2 concentration to B 2 O 3 concentration in the range between 1:1 and 30:1, within the temperature range of from 100°C below the softening point of the said borosilicate glass composition to the softening point of the said borosilicate glass composition so as to result in out-diffusion of boron oxide from the said borosilicate glass thereby producing (1) a core region of lesser boron oxide content than that of the corresponding region of the said borosilicate glass before processing, and (2) a clad region which is of a composition more nearly that of the corresponding region of the said borosilicate glass before processing in which the said body before processing includes 2 borosilicate surfaces and in which out-diffusion is smultaneously from the two surfaces.
Claim 2
Dependent Claim
223 words
Process for fabricating a light guide which as fabricated comprises a body including a core region and a clad region, the refractive index being graded from a first value within the core region to a lesser value within the clad region in which the variation in refractive index is due to an increasing content of boron oxide, said increasing content corresponding in direction with decreasing refractive index, in which both core region and clad region are constituted of glass comprising heat treating a body consisting essentially of a borosilicate glass composition, said composition having a ratio of SiO 2 concentration to B 2 O 3 concentration in the range between 1:1 and 30:1, within the temperature range of from 100°C below the softening point of the said borosilicate glass composition to the softening point of the said borosilicate glass composition so as to result in out-diffusion of boron oxide from the said borosilicate glass thereby producing (1) a core region of lesser boron oxide content than that of the corresponding region of the said borosilicate glass before processing, and (2) a clad region which is of a composition more nearly that of the corresponding region of the said borosilicate glass before processing in which the said body before processing includes 2 borosilicate surfaces and in which out-diffusion is smultaneously from the two surfaces.
Claim 3
Dependent Claim
41 words
Process of claim 1 in which the two said surfaces are the inner and outer surface of a tubular body so that out-diffusion results in increasing index of refraction corresponding to decreasing boron content at each of the two said surfaces.
Claim 4
Dependent Claim
225 words
Process for fabricating a light guide which as fabricated comprises a body including a core region and a clad region, the refractive index being graded from a first value within the core region to a lesser value within the clad region in which the variation in refractive index is due to an increasing content of boron oxide, said increasing content corresponding in direction with decreasing refractive index, in which both core region and clad region are constituted of glass comprising heat treating a body consisting essentially of a borosilicate glass composition, said composition having a ratio of SiO 2 concentration to B 2 O 3 concentration in the range between 1:1 and 30:1, within the temperature range of from 100°C below the softening point of the said borosilicate glass composition to the softening point of the said borosilicate glass composition so as to result in out-diffusion of boron oxide from the said borosilicate glass thereby producing (1) a core region of lesser boron oxide content than that of the corresponding region of the said borosilicate glass before processing, and (2) a clad region which is of a composition more nearly that of the corresponding region of the said borosilicate glass before processing in which the said body before processing includes a layer of borosilicate glass supported on a substrate, said layer having a free surface.
Claim 5
Dependent Claim
225 words
Process for fabricating a light guide which as fabricated comprises a body including a core region and a clad region, the refractive index being graded from a first value within the core region to a lesser value within the clad region in which the variation in refractive index is due to an increasing content of boron oxide, said increasing content corresponding in direction with decreasing refractive index, in which both core region and clad region are constituted of glass comprising heat treating a body consisting essentially of a borosilicate glass composition, said composition having a ratio of SiO 2 concentration to B 2 O 3 concentration in the range between 1:1 and 30:1, within the temperature range of from 100°C below the softening point of the said borosilicate glass composition to the softening point of the said borosilicate glass composition so as to result in out-diffusion of boron oxide from the said borosilicate glass thereby producing (1) a core region of lesser boron oxide content than that of the corresponding region of the said borosilicate glass before processing, and (2) a clad region which is of a composition more nearly that of the corresponding region of the said borosilicate glass before processing in which the said body before processing includes a layer of borosilicate glass supported on a substrate, said layer having a free surface.
Claim 6
Dependent Claim
45 words
Process of claim 3 in which regions of the free surface of the supported layer are masked so as to lessen out-diffusion in masked regions, thereby defining a pattern in the said glass which manifests index of refraction greater than that of the masked regions.
Claim 7
Dependent Claim
249 words
Process for fabricating a light guide which as fabricated comprises a body including a core region and a clad region, the refractive index being graded from a first value within the core region to a lesser value within the clad region in which the variation in refractive index is due to an increasing content of boron oxide, said increasing content corresponding in direction with decreasing refractive index, in which both core region and clad region are constituted of glass comprising heat treating a body consisting essentially of a borosilicate glass composition within the temperature range of from 100°C below the softening point of the said borosilicate glass composition to the softening point of the said borosilicate glass composition so as to result in out-diffusion of boron oxide from the said borosilicate glass thereby producing (1) a core region of lesser boron oxide content than that of the corresponding region of the said borosilicate glass before processing, and (2) a clad region which is of a composition more nearly that of the corresponding region of the said borosilicate glass before processing said composition before processing having a ratio of SiO 2 concentration to B 2 O 3 concentration in the range between 1:1 and 30:1 in which the said borosilicate glass is in the form of a tubular body before processing and in which a silica-base glass rod of index greater than that of the said inner surface of the said tube after processing is inserted within the tubular body.
Claim 8
Dependent Claim
249 words
Process for fabricating a light guide which as fabricated comprises a body including a core region and a clad region, the refractive index being graded from a first value within the core region to a lesser value within the clad region in which the variation in refractive index is due to an increasing content of boron oxide, said increasing content corresponding in direction with decreasing refractive index, in which both core region and clad region are constituted of glass comprising heat treating a body consisting essentially of a borosilicate glass composition within the temperature range of from 100°C below the softening point of the said borosilicate glass composition to the softening point of the said borosilicate glass composition so as to result in out-diffusion of boron oxide from the said borosilicate glass thereby producing (1) a core region of lesser boron oxide content than that of the corresponding region of the said borosilicate glass before processing, and (2) a clad region which is of a composition more nearly that of the corresponding region of the said borosilicate glass before processing said composition before processing having a ratio of SiO 2 concentration to B 2 O 3 concentration in the range between 1:1 and 30:1 in which the said borosilicate glass is in the form of a tubular body before processing and in which a silica-base glass rod of index greater than that of the said inner surface of the said tube after processing is inserted within the tubular body.
Claim 9
Dependent Claim
14 words
Process of claim 2 in which the tubular body is collapsed subsequent to out-diffusion.
Claim 10
Dependent Claim
26 words
Process of claim 6 in which the borosilicate glass while at an elevated temperature is exposed to a gaseous ambient which favors out-diffusion of boron oxide.
Claim 11
Dependent Claim
13 words
Process of claim 7 in which the said ambient comprises a flowing stream.
Claim 12
Dependent Claim
30 words
Process of claim 8 in which out-diffusion is favored by reaction between at least a component of the said gas with the said glass to produce a volatile boron-containing compound.
Claim 13
Dependent Claim
25 words
Process of claim 9 in which the said component comprises an agent selected from the group consisting of water, ammonia, alcohols, amines, and deuterated equivalents.
Claim 14
Dependent Claim
38 words
Process of claim 10 in which the said component consists essentially of an agent selected from the group consisting of H 2 O and D 2 O and in which the said elevated temperature is at least 700°C.
Claim 15
Dependent Claim
14 words
Process of claim 11 in which the said elevated temperature is at least 1,000°C.
Claim 16
Dependent Claim
21 words
Process of claim 6 in which the said borosilicate glass contains at least one additional ingredient which increases index of refraction.
Claim 17
Dependent Claim
22 words
Process of claim 13 in which said ingredient is selected from the group consisting of compounds of germanium, titanium, phosphorous and aluminum.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-15 | 1979-12-15 | 1980-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-15 | 1983-12-15 | 1984-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-15 | 1987-12-15 | 1988-06-15 | $7700.00 | Window Closed / Lapsed |