Assignee: PQ Corp
•
Filing: 1974-05-02
•
Granted: 1976-06-01
•
Expires: 1994-05-02
Abstract
Abstract Products of a generally spherical nature with particulate matter embedded in the walls are prepared by forming a suspension of said particulate matter in a solution of a film-forming substance in a volatile solvent, spray drying said suspension-solution thereby forming the product which may be further dried if necessary to remove solvent and to "set" the walls. Such products can be used to provide pigmenting, reactive and/or fire retardant properties to organic systems to which they are added as fillers. The density of the product can also be controlled by this method for use as fillers in applications in which segregation of such fillers from the plastic matrix is normally a problem.
Inventors
- 👤 David I. Netting
- 👤 Elliot P. Hertzenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:40
CPC Classifications
B; B01; B01J; B01J13/00; B01J13/02; B01J13/04; B01J13/043
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
166 words
The process for producing hollow spherical products of 1 to 500 microns with particulate matter imbedded in the walls, comprising the steps of; a. forming a solution of 5 to 50% film-forming substance consisting of sodium silicate and a polysalt selected from the group consisting of ammonium pentaborate, sodium pentaborate and sodium hexametaphosphate and 50 to 95% water, wherein the ratio of polysalt to silicate solids is between 0.02:1 and 3:1; b. introducing into said solution a particulate matter having a particle size of 0.05 to 10 microns which is substantially unreactive and insoluble in the solution; c. agitating said solution and particulate matter to produce a homogeneous suspension-solution, the amount of said particulate solids being sufficient to provide 0.5 to 75% of the solids contained in said suspension-solution; d. spray drying the suspension-solution at an inlet temperature of 200° to 500°C and an outlet temperature of 100° to 300°C; e. collecting the product having a true particle density of 20 to 200 lbs/ft 3 .
Claim 2
Dependent Claim
166 words
The process for producing hollow spherical products of 1 to 500 microns with particulate matter imbedded in the walls, comprising the steps of; a. forming a solution of 5 to 50% film-forming substance consisting of sodium silicate and a polysalt selected from the group consisting of ammonium pentaborate, sodium pentaborate and sodium hexametaphosphate and 50 to 95% water, wherein the ratio of polysalt to silicate solids is between 0.02:1 and 3:1; b. introducing into said solution a particulate matter having a particle size of 0.05 to 10 microns which is substantially unreactive and insoluble in the solution; c. agitating said solution and particulate matter to produce a homogeneous suspension-solution, the amount of said particulate solids being sufficient to provide 0.5 to 75% of the solids contained in said suspension-solution; d. spray drying the suspension-solution at an inlet temperature of 200° to 500°C and an outlet temperature of 100° to 300°C; e. collecting the product having a true particle density of 20 to 200 lbs/ft 3 .
Claim 3
Dependent Claim
48 words
The process of claim 1 wherein the polysalt is sodium hexametaphosphate, the suspension-solution includes 1.5 to 60% suspended particulate solids and 29.6 to 48% film-forming solids of sodium hexametaphosphate and sodium silicate, and the ratio of sodium hexametaphosphate solids to sodium silicate solids is between 1:1 and 3:1.
Claim 4
Dependent Claim
46 words
The process of claim 1 wherein the polysalt is sodium pentaborate, the suspension-solution includes 0.9 to 51.2% suspended particulate solids and 17.4 to 34.5% film-forming solids of sodium pentaborate and sodium silicate, and the ratio of sodium pentaborate solids to sodium silicate between 0.02:1 and 0.3:1.
Claim 5
Dependent Claim
52 words
The process of claim 1 wherein the polysalt is ammonium pentaborate, the suspension-solution includes 0.25 to 51.2% suspended particulate solids, and 5 to 34.5% film-forming solids of ammonium pentaborate and sodium silicate, and the ratio of ammonium pentaborate solids to ammonium pentaborate solids to ammonium pentaborate solids is between 0.03:1 and 0.5:1.
Claim 6
Dependent Claim
21 words
The process of claim 4 wherein the ratio of ammonium pentaborate solids to sodium silicate solids is between 0.06:1 and 0.5:1.
Claim 7
Dependent Claim
18 words
The process of claim 4 wherein the particulate matter has a particle size of 0.05 to 10 microns.
Claim 8
Dependent Claim
21 words
The process of claim 4 wherein the particulate matter is a pigment with a particle size between 0.05 and 6 microns.
Claim 9
Dependent Claim
63 words
The process of claim 7 wherein the suspension-solution includes 5 to 34.8% ammonium pentaborate and sodium silicate solids and 0.05 to 5.6% pigment solids selected from a group consisting of the oxides of iron, Chromium III, titanium, zinc and antimony, praseodynium zirconium silicate, vanadium zirconium silicate, talc, copper phthalocyanine, carbon black, nickel antimony titanate, cadmium sulfide, lead chromate, cobalt aluminate, and silicon carbide.
Claim 10
Dependent Claim
21 words
The process of claim 4 wherein the particulate matter is reactive and has a particle size of 0.5 to 5 microns.
Claim 11
Dependent Claim
44 words
The process of claim 9 wherein the suspension-solution includes 5 to 33.8% ammonium pentaborate-sodium silicate solids and 0.5 to 26% reactive particles selected from a group consisting of activated charcoal, zinc oxide, silica gel, magnesium oxide, zeolites, ferrites, molecular sieves, and ion exchange resins.
Claim 12
Dependent Claim
23 words
The process of claim 4 wherein the particulate matter is a fire retardant and has a particle size of 0.5 to 3 microns.
Claim 13
Dependent Claim
46 words
The process of claim 11 wherein the suspension-solution includes 5 to 31.5% ammonium pentaborate-sodium silicate solids and 1.2 to 51.2% fire retardant particles selected from a group consisting of antimony trioxide, antimony tetraoxide, combinations of antimony trioxide and talc, zinc borate, aluminum hydroxide and titanium dioxide.
Claim 14
Dependent Claim
51 words
The process of claim 6 wherein the suspension-solution includes 5 to 33% ammonium pentaborate-silicate solids and 2.8 to 51.2% particulate matter selected from a group consisting of magnesium oxide, alumina, zinc oxide, silica gel, calcium carbonate, calcium silicate (wollastonite), magnesium silicate (talc), barium sulfate, calcium sulfate, carbon black and ground glass.
Claim 15
Dependent Claim
17 words
The process of claim 6 wherein the particulate matter has a specific gravity of 2.2 to 5.7.
Claim 16
Dependent Claim
83 words
A hollow product of largely spherical nature with a particle size of 10 to 500 microns and a true particle density of 20 to 200 lbs/ft 3 consisting essentially of 25 to 99.5% film-forming substance consisting of sodium silicate and a polysalt selected from a group consisting of ammonium pentaborate, sodium pentaborate and sodium hexametaphosphate; 0.5 to 75% particulate matter embedded in the walls and 0 to 7% water with the ratio of polysalt solids to sodium silicate solids between 0.02:1 and 3:1.
Claim 17
Dependent Claim
83 words
A hollow product of largely spherical nature with a particle size of 10 to 500 microns and a true particle density of 20 to 200 lbs/ft 3 consisting essentially of 25 to 99.5% film-forming substance consisting of sodium silicate and a polysalt selected from a group consisting of ammonium pentaborate, sodium pentaborate and sodium hexametaphosphate; 0.5 to 75% particulate matter embedded in the walls and 0 to 7% water with the ratio of polysalt solids to sodium silicate solids between 0.02:1 and 3:1.
Claim 18
Dependent Claim
27 words
The product of claim 15 wherein the polysalt is sodium pentaborate and the ratio of sodium pentaborate solids to sodium silicate solids is between 0.02:1 and 0.3:1.
Claim 19
Dependent Claim
27 words
The product of claim 15 wherein the polysalt is sodium hexametaphosphate and the ratio of sodium hexametaphosphate solids to sodium silicate solids is between 1:1 and 3:1.
Claim 20
Dependent Claim
26 words
The product of claim 15 wherein the polysalt is ammonium pentaborate and the ratio of ammonium pentaborate solids to silicate solids is between 0.03:1 and 0.5:1.
Claim 21
Dependent Claim
21 words
The product of claim 18 wherein the ratio of ammonium pentaborate solids to sodium silicate solids is between 0.06:1 and 0.5:1.
Claim 22
Dependent Claim
83 words
The product of claim 18 wherein the product is pigmenting, has a true particle density of 20 to 40 lbs/ft 3 and consists essentially of 85 to 99% of ammonium pentaborate and sodium silicate 0 to 7% water and 1 to 15% particulate matter selected from a group consisting of the oxides of iron, chromium III, titanium, zinc and antimony; praseodynium zirconium silicates, vanadium zirconium silicate, talc, copper phthalocyanine, carbon black, nickel antimony titanate, cadmium sulfide, lead chromate, cobalt antimonate and silicon carbide.
Claim 23
Dependent Claim
61 words
The product of claim 18 wherein the product contains reactive particles, has a true particle density of 20 to 40 lbs/ft 3 and consists essentially of 50 to 90% ammonium pentaborate and sodium silicate, 0 to 7% water and 10 to 50% reactive particles selected from the group consisting of activated charcoal, zinc oxide, silica gel, magnesium oxide, zeolite and ferrites.
Claim 24
Dependent Claim
73 words
The product of claim 18 wherein the product contains fire retardant particles, has a true particle density of 25 to 81 lbs/ft 3 and consists essentially of 25 to 75% ammonium pentaborate and sodium silicate, 0 to 7% water and 25 to 75% fire retardant particles selected from a group consisting of antimony trioxide, antimony tetraoxide, combinations of antimony trioxide and talc, zinc borate, aluminum hydroxide, barium metaborate, zinc oxide and titanium dioxide.
Claim 25
Dependent Claim
69 words
The product of claim 18 wherein the true particle density is controlled between 31.2 and 200 lbs/ft 3 and consists essentially of 25 to 85% ammonium pentaborate and sodium silicate, 0 to 7% water and 15 to 75% particles selected from a group consisting of magnesium oxide, alumina, zinc oxide, silica gel, calcium carbonate, calcium silicate (wollastonite), magnesium silicate (talc), barium sulfate, calcium sulfate, carbon black and ground glass.
References Cited (Backward Citations)
US2555282A
Cited
US2797201A
Cited
US3561003A
Cited
US3607777A
Cited
US3779957A
Cited
US3796777A
Cited
US3794503A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-01 | 1979-12-01 | 1980-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-01 | 1983-12-01 | 1984-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-01 | 1987-12-01 | 1988-06-01 | $7700.00 | Window Closed / Lapsed |