Cross-linking agents for room temperature vulcanizable silicone rubber compositions

Claim 2

A cross-linking agent for room temperature vulcanizable silicone rubber compositions comprising the reaction product of 25 to 75 parts of a silicate selected from the class consisting of silicates of the formula, R.sub.a.sup.2 Si(OR.sup.1).sub.4.sub.-a, and a liquid partial hydrolysis product of the aforementioned alkyl silicates and 10 to 40 parts of a polysiloxane fluid of the formula, R.sub.n.sup.3 SiO.sub.4.sub.-n/2, where the polysiloxane fluid is chain-stopped with mixtures of --OH groups and R 3 3 SiO 1/2 units, where the ratio of the R 3 3 SiO 1/2 units to --OH groups in the fluid varies from 3:1 to 1:1 and a metal salt of an acid selected from the class consisting of monocarboxylic acid and dicarboxylic acid and the metal ion is selected from the class consisting of lead, tin, zirconium, antimony, iron, cadmium, barium, calcium, titanium, bismuth and manganese, where R 1 , R 2 and R 3 are selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and mixtures thereof, a is 0 or 1, and varies from 1.9 to 2.1.

Claim 3

The cross-linking agent of claim 1 wherein R 3 is methyl, the metal salt is a tin salt of a monocarboxylic acid, and the polysiloxane fluid has a viscosity that varies from 100 to 10,000 centipoise at 25°C.

Claim 4

The cross-linking agent of claim 1 wherein the silicate is selected from the class consisting of silicates of the formula, (R.sup.1 O).sub.4 Si, and partial liquid hydrolysis products thereof, and R 1 is ethyl.

Claim 5

The cross-linking agent of claim 1 wherein the polysiloxane fluid contains at least 90 mole percent of difunctional units and up to 10 mole percent of monofunctional units and trifunctional units.

Claim 6

The cross-linking agent of claim 1 wherein R 1 , R 2 and R 3 are selected from the class consisting of alkyl radicals of 1 to 8 carbon atoms, alkenyl radicals of 2 to 8 carbon atoms, cycloalkyl radicals of 4 to 8 carbon atoms and mononuclear aryl, alkaryl radicals of up to 10 carbon atoms and halogenated derivatives of the foregoing radicals.

Claim 7

The cross-linking agent of claim 1 wherein in the polysiloxane fluid the ratio of R 3 3 SiO 1/2 units to --OH radicals is 1:1 and R 3 is methyl.

Claim 8

A process for producing a cross-linking agent for room temperature vulcanizable silicone rubber compositions comprising reacting at a temperature in the range of 70° to 180°C, a mixture containing from 25 to 75 parts of a silicate selected from the class consisting of silicates of the formula, R.sub.a.sup.2 Si(OR.sup.1).sub.4.sub.-a, and liquid partial hydrolysis products of the aforementioned silicate, 10 to 40 parts of a polysiloxane fluid of the formula, R.sub.n.sup.3 SiO.sub.4.sub.-n/2 where the polysiloxane fluid is chain-stopped with mixtures of --OH groups and R 3 3 SiO 1/2 units, wherein the ratio of R 3 3 SiO 1/2 units to --OH groups in the fluid radicals varies from 3:1 to 1:1 and 10 to 40 parts of a tin salt of an acid selected from the class consisting of monocarboxylic acid and dicarboxylic acid, where R 1 , R 2 and R 3 are selected from the class consisitng of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and mixtures thereof, where a is 0 or 1, and n varies from 1.9 to 2.1.

Claim 9

A process for producing a cross-linking agent for room temperature vulcanizable silicone rubber compositions comprising reacting at a temperature in the range of 70° to 180°C, a mixture containing from 25 to 75 parts of a silicate selected from the class consisting of silicates of the formula, R.sub.a.sup.2 Si(OR.sup.1).sub.4.sub.-a, and liquid partial hydrolysis products of the aforementioned silicate, 10 to 40 parts of a polysiloxane fluid of the formula, R.sub.n.sup.3 SiO.sub.4.sub.-n/2 where the polysiloxane fluid is chain-stopped with mixtures of --OH groups and R 3 3 SiO 1/2 units, wherein the ratio of R 3 3 SiO 1/2 units to --OH groups in the fluid radicals varies from 3:1 to 1:1 and 10 to 40 parts of a tin salt of an acid selected from the class consisting of monocarboxylic acid and dicarboxylic acid, where R 1 , R 2 and R 3 are selected from the class consisitng of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and mixtures thereof, where a is 0 or 1, and n varies from 1.9 to 2.1.

Claim 10

The process of claim 7 wherein the reaction is carried out for a period varying from 20 minutes to 8 hours.

Claim 11

The process of claim 7 wherein the reaction is preferably carried out at a temperature in the range of 130° to 140°C.

Claim 12

The process of claim 7 wherein the silicate is present at a concentration of 40 to 60 parts, the polysiloxane fluid is present at a concentration of 20 to 30 parts and the tin salt is present at a concentration of 20 to 30 parts.

Claim 13

The process of claim 7 wherein R 3 is methyl and the polysiloxane fluid has a viscosity that varies from 100 to 10,000 centipoise at 25°C.

Claim 14

The process of claim 7 wherein the silicate is selected from the class consisting of silicates of the formula, (R.sup.1 O).sub.4 Si, and partial liquid hydrolysis products thereof and R 1 is ethyl.

Claim 15

The process of claim 7 wherein the polysiloxane fluid contains at least 90 mole percent of difunctional units and up to 10 mole percent of monofunctional units and trifunctional units.

Claim 16

The process of claim 7 wherein R 1 , R 2 and R 3 are selected from the class consisting of alkyl radicals of 1 to 8 carbon atoms, cycloalkyl radicals of 4 to 8 carbon atoms, alkenyl radicals of 2 to 8 carbon atoms and mononuclear aryl, alkaryl radicals of up to 10 carbon atoms and halogenated derivatives of the foregoing radicals.

Claim 17

The process of claim 7 wherein the polysiloxane fluid the ratio of R 3 3 SiO 1/2 units to --OH radicals is 1:1 and R 3 is methyl.

Claim 18

A room temperature vulcanizable silicone rubber composition comprising (a) a diorganopolysiloxane containing terminal-bonded hydroxy groups having a viscosity varying from 1,000 to 10,000,000 centipoise at 25°C, where the organo group is selected from the class consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals and cyanoalkyl radicals, (b) from 5% to 300% by weight, based on the diorganopolysiloxane, of a filler, and (c) from 2% to 30% by weight based on the weight of (a) and (b) of a cross-linking agent which is the reaction product of 25 to 75 parts of a silicate selected from the class consisting of silicates of the formula, R.sub.a.sup.2 Si(OR.sup.1).sub.4.sub.-a, and liquid partial hydrolysis products of the aforementioned silicate, 10 to 40 parts of a polysiloxane fluid of the formula, R.sub.n.sup.3 SiO.sub.4.sub.-n/2, where the polysiloxane fluid is chain-stopped with mixtures of --OH groups and R 3 3 SiO 1/2 units, where the ratio of R 3 3 SiO 1/2 units to --OH groups in the fluid radicals varies from 3:1 to 1:1 and 10 to 40 parts of a metal salt of an acid selected from the class consisting of monocarboxylic acid, dicarboxylic acid and the metal ion is selected from the class consisting of lead, tin, zirconium, antimony, iron, cadmium, barium, calcium, titanium, bismuth and manganese, R 1 , R 2 and R 3 are selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and mixtures thereof, where a is 0 or 1, and n varies from 1.9 to 2.1.

Claim 19

A room temperature vulcanizable silicone rubber composition comprising (a) a diorganopolysiloxane containing terminal-bonded hydroxy groups having a viscosity varying from 1,000 to 10,000,000 centipoise at 25°C, where the organo group is selected from the class consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals and cyanoalkyl radicals, (b) from 5% to 300% by weight, based on the diorganopolysiloxane, of a filler, and (c) from 2% to 30% by weight based on the weight of (a) and (b) of a cross-linking agent which is the reaction product of 25 to 75 parts of a silicate selected from the class consisting of silicates of the formula, R.sub.a.sup.2 Si(OR.sup.1).sub.4.sub.-a, and liquid partial hydrolysis products of the aforementioned silicate, 10 to 40 parts of a polysiloxane fluid of the formula, R.sub.n.sup.3 SiO.sub.4.sub.-n/2, where the polysiloxane fluid is chain-stopped with mixtures of --OH groups and R 3 3 SiO 1/2 units, where the ratio of R 3 3 SiO 1/2 units to --OH groups in the fluid radicals varies from 3:1 to 1:1 and 10 to 40 parts of a metal salt of an acid selected from the class consisting of monocarboxylic acid, dicarboxylic acid and the metal ion is selected from the class consisting of lead, tin, zirconium, antimony, iron, cadmium, barium, calcium, titanium, bismuth and manganese, R 1 , R 2 and R 3 are selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and mixtures thereof, where a is 0 or 1, and n varies from 1.9 to 2.1.

Claim 20

The composition of claim 16 wherein in (c) the silicate is present at a concentration of 40 to 60 parts, the polysiloxane fluid is present at a concentration of 20 to 30 parts and the metal salt is present at a concentration of 20 to 30 parts.

Claim 21

The composition of claim 16 wherein in (c) R 3 is methyl, the metal salt is a tin salt of a monocarboxylic acid and the polysiloxane has a viscosity that varies from 100 to 10,000 centipoise at 25°C.

Claim 22

The composition of claim 16 wherein in (c) the silicate is selected from the class consisting of silicates of the formula, (R.sup.1 O).sub.4 Si, and partial liquid hydrolysis products thereof, and R 1 is ethyl.

Claim 23

The composition of claim 16 wherein in (c) the polysiloxane fluid contains at least 90 mole percent of difunctional units and up to 10 mole percent of monofunctional units and trifunctional units.

Claim 24

The composition of claim 16 wherein R 1 , R 2 and R 3 are selected from the class consisting of alkyl radicals of 1 to 8 carbon atoms, alkenyl radicals of 2 to 8 carbon atoms, cycloalkyl radicals of 4 to 8 carbon atoms and mononuclear aryl, alkaryl radicals of up to 10 carbon atoms and halogenated derivatives of the foregoing radicals.

Claim 25

The composition of claim 16 wherein in (c) in the polysiloxane fluid the ratio of R 3 3 SiO 1/2 units to --OH radicals is 1:1 and R 3 is methyl.