Glass-ceramics containing fibers exhibiting thermoplastic properties
Assignee: Corning Glass Works
•
Filing: 1974-08-01
•
Granted: 1976-02-24
•
Expires: 1994-08-01
Abstract
Abstract The present invention relates to the production of glass-ceramic articles having compositions within the alkali silicate field which, because the crystal phase consists essentially of silica fibers, demonstrates exceptional impact resistance. When such articles are subjected to steam hydration at elevated temperatures, toughness with accompanying resilience and thermoplastic behavior will be observed.
Inventors
- 👤 Joseph E. Pierson
- 👤 Stanley D. Stookey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:38
CPC Classifications
C; C03; C03C; C03C10/00; C03C10/0009
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
55 words
A glass-ceramic body exhibiting exceptional impact resistance consisting essentially of crystalline silica fibers contained within a residual glassy matrix, said fibers having a needlelike structure and being oriented in essentially a single direction, and said glass-ceramic body consisting essentially, by weight, of about 75-95% SiO 2 and 5-25% Na 2 O and/or K 2 O.
Claim 2
Dependent Claim
55 words
A glass-ceramic body exhibiting exceptional impact resistance consisting essentially of crystalline silica fibers contained within a residual glassy matrix, said fibers having a needlelike structure and being oriented in essentially a single direction, and said glass-ceramic body consisting essentially, by weight, of about 75-95% SiO 2 and 5-25% Na 2 O and/or K 2 O.
Claim 3
Dependent Claim
68 words
A glass-ceramic body according to claim 1 wherein said glass-ceramic body also contains up to 20% by weight total of at least one oxide in the indicated proportions selected from the group consisting of up to 5% Al 2 O 3 , CaO, Li 2 O, and/or TiO 2 , up to 10% BaO, SrO, B 2 O 3 , MgO, and/or ZnO, and up to 20% PbO.
Claim 4
Independent Claim
117 words
A method for making a glass-ceramic body consisting essentially of crystalline silica fibers contained within a residual glassy matrix and exhibiting exceptional impact resistance, said fibers having a needle-like structure and being oriented in essentially a single direction, which comprises: melting a batch for a glass consisting essentially, by weight, of about 5-25% Na 2 O and/or K 2 O and 75-95% SiO 2 ; b. simultaneously cooling and shaping a glass body therefrom; and c. exposing said glass body to a temperature between about 775°-1200°C. for a sufficient length of time to cause the crystallization of silica fibers therein, thereby making a glass-ceramic body consisting essentially of crystalline silica fibers contained in a residual glassy matrix.
Claim 5
Independent Claim
117 words
A method for making a glass-ceramic body consisting essentially of crystalline silica fibers contained within a residual glassy matrix and exhibiting exceptional impact resistance, said fibers having a needle-like structure and being oriented in essentially a single direction, which comprises: melting a batch for a glass consisting essentially, by weight, of about 5-25% Na 2 O and/or K 2 O and 75-95% SiO 2 ; b. simultaneously cooling and shaping a glass body therefrom; and c. exposing said glass body to a temperature between about 775°-1200°C. for a sufficient length of time to cause the crystallization of silica fibers therein, thereby making a glass-ceramic body consisting essentially of crystalline silica fibers contained in a residual glassy matrix.
Claim 6
Dependent Claim
66 words
A method according to claim 3 wherein said glass also contains up to 20% by weight total of at least one oxide in the indicated proportions selected from the group consisting of up to 5% Al 2 O 3 , CaO, Li 2 O, and/or TiO 2 , up to 10% BaO, MgO, SrO, B 2 O 3 , and/or ZnO, and up to 20% PbO.
Claim 7
Dependent Claim
22 words
A method according to claim 3 wherein said glass body is exposed to a temperature between about 775°-1200°C. for about 2-74 hours.
Claim 8
Dependent Claim
83 words
A glass-ceramic body exhibiting toughness and thermoplastic properties consisting essentially of crystalline silica fibers contained within a residual glassy matrix, said fibers having a needle-like structure and being oriented in essentially a single direction, wherein said glass-ceramic body has an amount of water absorbed therein effective to impart thermoplastic properties thereto, said glass-ceramic body consisting essentially, by weight on the oxide basis, exclusive of water contained within its volume, of about 75-95% SiO 2 and 5-25% Na 2 O and/or K 2 O.
Claim 9
Dependent Claim
83 words
A glass-ceramic body exhibiting toughness and thermoplastic properties consisting essentially of crystalline silica fibers contained within a residual glassy matrix, said fibers having a needle-like structure and being oriented in essentially a single direction, wherein said glass-ceramic body has an amount of water absorbed therein effective to impart thermoplastic properties thereto, said glass-ceramic body consisting essentially, by weight on the oxide basis, exclusive of water contained within its volume, of about 75-95% SiO 2 and 5-25% Na 2 O and/or K 2 O.
Claim 10
Dependent Claim
26 words
A glass-ceramic body according to claim 6 wherein the amount of water absorbed in said residual glassy matrix ranges up to about 35% by weight thereof.
Claim 11
Dependent Claim
26 words
A glass-ceramic body according to claim 6 wherein the amount of water absorbed in said residual glassy matrix does not exceed about 10% by weight thereof.
Claim 12
Dependent Claim
68 words
A glass-ceramic body according to claim 6 wherein said glass-ceramic body also contains up to 20% by weight total of at least one oxide in the indicated proportions selected from the group consisting of up to 5% Al 2 O 3 , CaO, Li 2 O, and/or TiO 2 , up to 10% BaO, MgO, SrO, B 2 O 3 , and/or ZnO, and up to 20% PbO.
Claim 13
Independent Claim
182 words
A method for making a glass-ceramic body consisting essentially of crystalline silica fibers contained within a residual glassy matrix and exhibiting toughness and thermoplastic properties, said fibers having a needle-like structure and being oriented in essentially a single direction, which comprises: a. melting a batch for a glass consisting essentially, by weight on the oxide basis, of about 5-25% Na 2 O and/or K 2 O and 75-95% SiO 2 ; b. simultaneously cooling and shaping a glass body therefrom; c. exposing said glass body to a temperature between about 775°-1200°C. for a sufficient length of time to cause the crystallization of silica fibers therein, thereby making a glass-ceramic body consisting essentially of crystalline silica fibers contained within a residual glassy matrix; and d. subjecting said glass-ceramic body to a H 2 O-containing environment of at least 10% relative humidity at a temperature greater than 100°C. for a sufficient length of time to cause an amount of water to be absorbed by said residual glassy matrix in at least a surface portion of said glass-ceramic article effective to impart thermoplastic properties thereto.
Claim 14
Independent Claim
182 words
A method for making a glass-ceramic body consisting essentially of crystalline silica fibers contained within a residual glassy matrix and exhibiting toughness and thermoplastic properties, said fibers having a needle-like structure and being oriented in essentially a single direction, which comprises: a. melting a batch for a glass consisting essentially, by weight on the oxide basis, of about 5-25% Na 2 O and/or K 2 O and 75-95% SiO 2 ; b. simultaneously cooling and shaping a glass body therefrom; c. exposing said glass body to a temperature between about 775°-1200°C. for a sufficient length of time to cause the crystallization of silica fibers therein, thereby making a glass-ceramic body consisting essentially of crystalline silica fibers contained within a residual glassy matrix; and d. subjecting said glass-ceramic body to a H 2 O-containing environment of at least 10% relative humidity at a temperature greater than 100°C. for a sufficient length of time to cause an amount of water to be absorbed by said residual glassy matrix in at least a surface portion of said glass-ceramic article effective to impart thermoplastic properties thereto.
Claim 15
Dependent Claim
66 words
A method according to claim 10 wherein said glass also contains up to 20% by weight total of at least one oxide in the indicated proportions selected from the group consisting of up to 5% Al 2 O 3 , CaO, Li 2 O, and/or TiO 2 , up to 10% BaO, MgO, SrO, B 2 O 3 , and/or ZnO, and up to 20% PbO.
Claim 16
Dependent Claim
22 words
A method according to claim 10 wherein said glass body is exposed to a temperature between about 775°-1200°C. for about 2-72 hours.
Claim 17
Dependent Claim
18 words
A method according to claim 10 wherein said glass-ceramic body is subjected to a 100% relative humidity environment.
Claim 18
Dependent Claim
33 words
A method according to claim 10 wherein said glass-ceramic body is subjected to a H 2 O-containing environment at temperatures ranging from about 100°C. up to about the deformation point of the body.
Claim 19
Dependent Claim
22 words
A method according to claim 10 wherein said glass-ceramic body is subjected to a H 2 O-containing environment for about 2-24 hours.
Claim 20
Dependent Claim
56 words
A method for forming shapes from the hydrated glass-ceramic body made in accordance with claim 10 exhibiting thermoplastic properties which comprises the steps of: a. forming said body to a shape of a desired configuration under pressure and at a temperature ranging between about 100°-500°C.; and, thereafter, b. bringing said shape to room temperature and pressure.
Claim 21
Dependent Claim
16 words
A method according to claim 16 wherein said shape is formed at temperatures between about 100°-400°C.
References Cited (Backward Citations)
US3450546A
Cited
US3445252A
Cited
US3498803A
Cited
US3498802A
Cited
US3776809A
Cited
US3464807A
Cited
US3804608A
Cited
US3713854A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-23 | 1979-08-25 | 1980-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-23 | 1983-08-25 | 1984-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-23 | 1987-08-25 | 1988-02-24 | $7700.00 | Window Closed / Lapsed |